Investigation on transition behavior and electrical properties of (K{sub 0.5}Na{sub 0.5}){sub 1-x}Li{sub x}Nb{sub 0.84}Ta{sub 0.1}Sb{sub 0.06}O{sub 3} around polymorphic phase transition region
- Department of Physics, Renmin University of China, Beijing 100872, P R China (China)
- Key Laboratory of Optoelectronic Materials Chemistry and Physics, Fujian Institute of Research on the Structure of Matter, Chinese Academy of Sciences, Fuzhou 350002 (China)
- School of Chemistry and Environment Engineering, Shaoguan University, Shaoguan 512005 (China)
(K{sub 0.5}Na{sub 0.5}){sub 1-x}Li{sub x}Nb{sub 0.84}Ta{sub 0.1}Sb{sub 0.06}O{sub 3} (KNLNTS) lead free ceramics with different Li concentration were fabricated by conventional solid-state reaction method. By increasing Li ions in KNLNTS, the grains grow up and the crystal structure changes from orthorhombic to tetragonal. When 0.03 ≤ x ≤ 0.05, the ceramics structure lays in PPT region. Polarization versus electric field (P-E) hysteresis loops at room temperature show good ferroelectric properties and the remnant polarization decreases by increasing Li content while coercive electric keeps almost unchanged. In PPT region, taking x = 0.04 as an example, the sample shows excellent dielectric properties: the dielectric constant is 1159 and loss tangent is 0.04, while the piezoelectric constant d{sub 33} is 245 pC/N and kp is 0.44 at room temperature, it is promising for (K{sub 0.5}Na{sub 0.5}){sub 1-x}Li{sub x}Nb{sub 0.84}Ta{sub 0.1}Sb{sub 0.06}O{sub 3} with 4 at. % Li to substitute PZT.
- OSTI ID:
- 22251615
- Journal Information:
- AIP Advances, Journal Name: AIP Advances Journal Issue: 1 Vol. 4; ISSN AAIDBI; ISSN 2158-3226
- Country of Publication:
- United States
- Language:
- English
Similar Records
Doping effects of Li-Sb content on the structure and electrical properties of [(Na{sub 0.5}K{sub 0.5}){sub 1-x}(Li){sub x}(Sb){sub x}(Nb){sub 1} {sub -x}O{sub 3}] lead-free piezoelectric ceramics
Crystal structure analysis of lead free Ba{sub 1-x}La{sub x}[Ti{sub 0.5}(Fe{sub 0.5}Nb{sub 0.5}){sub 0.5}]{sub 1-x/4}O{sub 3} Ceramics