Full phosphorescent white-light organic light-emitting diodes with improved color stability and efficiency by fine tuning primary emission contributions
- Key Laboratory of Interface Science and Engineering in Advanced Materials, Taiyuan University of Technology, Ministry of Education, Taiyuan 030024 (China)
- Printable Electronics Research Centre, Suzhou Institute of Nano-Tech and Nano-Bionics, CAS, suzhou 215123 (China)
In this paper, a novel type of white-light organic light emitting diode (OLED) with high color stability was reported, in which the yellow-light emission layer of (4,4{sup ′}-N,N{sup ′}-dicarbazole)biphenyl (CBP) : tris(2-phenylquinoline-C2,N{sup ′})iridium(III) (Ir(2-phq){sub 3}) was sandwiched by double blue-light emission layers of 1,1-bis-[(di-4-tolylamino)pheny1]cyclohexane (TAPC) : bis[4,6-(di-fluorophenyl)-pyridinato-N,C2{sup ′}]picolinate (FIrpic) and tris[3-(3-pyridyl)mesityl]borane (3TPYMB):FIrpic. And, it exhibited the maximum current efficiency of 33.1 cd/A, the turn-on voltage at about 3 V and the maximum luminance in excess of 20000 cd/m{sup 2}. More important, it realized very stable white-light emission, and its CIE(x, y) coordinates only shift from (0.34, 0.37) to (0.33, 0.37) as applied voltage increased from 5 V to 12 V. It is believed that the new scheme in emission layer of white-light OLED can fine tune the contribution of primary emission with applied voltage changed, resulting in high quality white-light OLED.
- OSTI ID:
- 22251561
- Journal Information:
- AIP Advances, Journal Name: AIP Advances Journal Issue: 2 Vol. 4; ISSN AAIDBI; ISSN 2158-3226
- Country of Publication:
- United States
- Language:
- English
Similar Records
High efficiency and low roll-off blue phosphorescent organic light-emitting devices using mixed host architecture
Ultraviolet Electroluminescence and Blue-Green Phosphorescence using an Organic Diphosphine Oxide Charge Transporting Layer.
Designing Organic Phosphine Oxide Host Materials Using Heteroaromatic Building Blocks: Inductive Effects on Electroluminescence
Journal Article
·
Tue Jul 20 00:00:00 EDT 2010
· Applied Physics Letters, 97:033304
·
OSTI ID:991568
Ultraviolet Electroluminescence and Blue-Green Phosphorescence using an Organic Diphosphine Oxide Charge Transporting Layer.
Journal Article
·
Mon May 01 00:00:00 EDT 2006
· Applied Physics Letters, 88:Art. no. 183503
·
OSTI ID:885462
Designing Organic Phosphine Oxide Host Materials Using Heteroaromatic Building Blocks: Inductive Effects on Electroluminescence
Conference
·
Sun Nov 18 23:00:00 EST 2007
·
OSTI ID:928284