Development of Composite Adsorbents for LLW Treatment and Their Adsorption Properties for Cs and Sr - 13127
- Dept. of Quantum Science and Energy Engineering, Graduate School of Engineering, Tohoku University, Aramaki-Aza-Aoba 6-6-01-2, Sendai, 980-8579 (Japan)
- Nuclear Science and Engineering Directorate, Japan Atomic Energy Agency, 2-4 Shirakata Shirone, Naka-gun, Ibaraki, 319-1195 (Japan)
In this study, the composite adsorbents (KCoFC-NM (NM: natural mordenite), KCoFC-SG (SG: porous silica gel), AMP-SG and so on) were prepared by impregnation-precipitation methods. As for the distribution properties, the largest K{sub d,Cs} value of 3.8 x 10{sup 4} cm{sup 3}/g was obtained for KCoFC-SG (Davi.) composite. KCoFC-SG (NH, MB5D) and T-KCFC also had relatively large K{sub d,Cs} values above 1.0 x 10{sup 4} cm{sup 3}/g. The uptake rate of Cs{sup +} ions was examined by batch method. KCoFC-SG (NH, MB5D) and AMP-SG (Davi.) had relatively large uptake rate of Cs{sup +}, and the uptake attained equilibrium within 1 h. The maximum uptake capacity of Cs{sup +} ions was estimated to be above 0.5 mmol/g for KCoFC-NM and KCoFC-CP composites. KCoFC-X composite had a relatively large uptake capacity of Cs{sup +} ions (0.23 mmol/g > 0.17 mmol/g (T-KCFC)) and this composite also had a selectivity towards Sr{sup 2+} ions; KCoFC-X is effective adsorbent for both Cs{sup +} and Sr{sup 2+} ions. The largest value of K{sub d,Sr} was estimated to be 218 cm{sup 3}/g for titanic acid-PAN. Titanic acid-PAN had the largest uptake rate of Sr{sup 2+} ions, and the uptake attained equilibrium within 8 h. Adsorbability of other nuclides was further examined by batch method. All adsorbents had adsorbability for Rb{sup +} and RuNO{sup 3+} ions. KCoFC-SG (NH), KCoFC-CP and T-KCFC had higher selectivity towards Cs{sup +} than other adsorbents; these adsorbents had adsorbability to Cs{sup +} ions even in the presence of Ba{sup 2+}, Ca{sup 2+} and Mg{sup 2+} ions. The separation factor of K{sub d,Sr}/K{sub d,Ba} for titanic acid-PAN was about 1, indicating that the K{sub d,Sr} for titanic acid-PAN tends to decrease with Ba{sup 2+} concentration. As for the breakthrough properties, the largest 5 % breakpoint and 5 % breakthrough capacity of Cs{sup +} ions were estimated to be 47.1 cm{sup 3} and 0.07 mmol/g for the column of KCoFC-SG (NH), respectively. The order of 5 % breakthrough capacity of Cs{sup +} is as follows; KCoFC-SG (NH) > KCoFC-NM > KCoFC-SG (Q-10) > T-KCFC > KCoFC-X > KCoFC-CP. From the results of batch and column experiments, the composite adsorbent of KCoFC-SG (NH) was effective for the uptake of Cs{sup +} ions, and KCoFC-X composite was useful for the uptake of both Cs{sup +} and Sr{sup 2+} ions. The estimation of irradiation stability and the uptake properties using the actual wastes are further essential for the practical operation. (authors)
- Research Organization:
- WM Symposia, 1628 E. Southern Avenue, Suite 9-332, Tempe, AZ 85282 (United States)
- OSTI ID:
- 22224908
- Report Number(s):
- INIS-US-13-WM-13127; TRN: US14V0347045863
- Resource Relation:
- Conference: WM2013: Waste Management Conference: International collaboration and continuous improvement, Phoenix, AZ (United States), 24-28 Feb 2013; Other Information: Country of input: France; 7 refs.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Adsorption properties of Cs{sup +} for composite adsorbents and their irradiation stabilities
Sorption of cesium and strontium from concentrated brines by backfill barrier materials