Adhesion strength of sputtered TiAlN-coated WC insert tool
- Department of Physics, Faculty of Science and Mathematics, Universitas Negeri Jakarta, Jl. Pemuda No. 10, Jakarta 13220 (Indonesia)
- Faculty of Manufacturing Engineering, Universiti Teknikal Malaysia Melaka Karung Berkunci No 1752 Pejabat Pos Durian Tunggal 76109 Melaka (Malaysia)
The adhesion strength of TiAlN coating that deposited by using DC magnetron sputtering on WC insert tool are studied. TiAlN coating are deposited on Tungsten Carbide (WC) insert tool by varying negatively substrate bias from 79 to 221 volt and nitrogen flow rate from 30 to 72 sccm. The adhesion strength are obtained by using Rockwell indentation test method with a Brale diamond at applied load of 60,100 and 150 kgf. The lateral diameter of indentation is plotted on three different applied loads and the adhesion strength of TiAlN coating was obtained from the curved slopes at 100 and 150 kgf. The lower curve slop indicated better adhesion strength. The results shows that the adhesion strength of sputterred TiAlN coating tend to increase as the negatively substrate bias and nitrogen flow rate are increased.
- OSTI ID:
- 22218078
- Journal Information:
- AIP Conference Proceedings, Vol. 1554, Issue 1; Conference: PIPS-2013: Padjadjaran international physics symposium 2013: Contribution of physics on environmental and energy conservations, Padjadjaran (Indonesia), 7-9 May 2013; Other Information: (c) 2013 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effect of Reactive Sputtering Parameters on TiAlN Nanocoating Structure and Morphology
Adhesion study of DLC/Cr/DLC and DLC/Ti/DLC sandwich structures on hardened steel