Color tunable and thermally stable luminescence of Tb{sup 3+} doped Li{sub 4}SrCa(SiO{sub 4}){sub 2} phosphors
Journal Article
·
· Materials Research Bulletin
- College of Materials Science and Engineering, Central South University of Forestry and Technology, Changsha 410004 (China)
Highlights: ► Lowest spin-allowed and spin-forbidden f–d transitions locate at 250 and 280 nm. ► Cross relaxation shortens lifetime of {sup 5}D{sub 3} level, while that of {sup 5}D{sub 4} are unaffected. ► Cross-relaxation can explain concentration quenching of the {sup 5}D{sub 3} emission. ► Dipole–quadrupole interaction is responsible for the non-radiative relaxation. ► Li{sub 4}SrCa(SiO{sub 4}){sub 2}:Tb{sup 3+} is thermally stable and color tunable phosphor. -- Abstract: Tb{sup 3+} ions activated Li{sub 4}SrCa(SiO{sub 4}){sub 2} phosphors were synthesized using a solid state reaction method. The phase impurity was checked by XRD. The photoluminescence (PL) excitation spectrum, emission spectra at room and high temperature, decay curves of samples with different Tb{sup 3+} ions concentration were studied in detail. Cross-relaxation and the Inokuti–Hirayama model were used to analyze the experimental results. Li{sub 4}SrCa(SiO{sub 4}){sub 2}:xTb{sup 3+} are thermally stable and color tunable phosphors.
- OSTI ID:
- 22215181
- Journal Information:
- Materials Research Bulletin, Journal Name: Materials Research Bulletin Journal Issue: 8 Vol. 47; ISSN MRBUAC; ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
Photoluminescence performance of thulium doped Li{sub 4}SrCa(SiO{sub 4}){sub 2} under irradiation of ultraviolet and vacuum ultraviolet lights
Visible quantum cutting through downconversion in GdPO{sub 4}:Tb{sup 3+} and Sr{sub 3}Gd(PO{sub 4}){sub 3}:Tb{sup 3+}
Observation on long afterglow of Tb{sup 3+} in CaWO{sub 4}
Journal Article
·
Fri Nov 14 23:00:00 EST 2014
· Materials Research Bulletin
·
OSTI ID:22420632
Visible quantum cutting through downconversion in GdPO{sub 4}:Tb{sup 3+} and Sr{sub 3}Gd(PO{sub 4}){sub 3}:Tb{sup 3+}
Journal Article
·
Sat Aug 15 00:00:00 EDT 2009
· Journal of Solid State Chemistry
·
OSTI ID:21370543
Observation on long afterglow of Tb{sup 3+} in CaWO{sub 4}
Journal Article
·
Wed Dec 14 23:00:00 EST 2011
· Materials Research Bulletin
·
OSTI ID:22212369