Hydroxide precursors to produce nanometric YCrO{sub 3}: Characterization and conductivity analysis
- Universidad Nacional Autónoma de México, Centro de Nanociencias y Nanotecnología, Km. 107 Carretera Tijuana-Ensenada, Apartado Postal 14, C.P. 22800, Ensenada, B.C. (Mexico)
Highlights: ► Y/Cr mixed hydroxide was precipitated with gaseous ammonia. ► The hydroxide treated at 1373 K formed YCrO{sub 3} crystals with 20 nm diameter. ► Electrical properties were different than those found in other methods of synthesis. ► E{sub act} suggests small-polarons as conduction mechanisms. -- Abstract: A precursor to produce perovskite-type YCrO{sub 3} was precipitated by bubbling gaseous ammonia into an yttrium/chromium salts solution. X-ray diffraction showed that the as-prepared powders were amorphous. Thermal treatment between 1273 and 1373 K, leads to formation of polycrystalline YCrO{sub 3} with crystal sizes around 20 nm. High resolution X-ray photoelectron spectra showed uniform chemical environment for yttrium and chromium in the amorphous hydroxide and crystalline YCrO{sub 3}. Shifts between Y 3d{sub 5/2} and Cr 2p{sub 3/2} binding energy suggest redistribution or charge transfer between yttrium and chromium ions in the YCrO{sub 3} structure. The electrical properties of YCrO{sub 3}, whose precursors were precipitated with gaseous ammonia are different than those prepared by combustion synthesis. Electrical conductivity presents a sudden increase at ∼473 K, which is associated to the grain size and morphology of the crystallites. The redistribution of charge between Y(III) and Cr(III) is thermally activated by the hopping of small-polarons, which are characterized by the Arrhenius law as the conductive mechanism.
- OSTI ID:
- 22215110
- Journal Information:
- Materials Research Bulletin, Vol. 47, Issue 6; Other Information: Copyright (c) 2012 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effects of cation substitution on electrical and thermal transport properties of YCrO/sub 3/ and LaCrO/sub 3/
Magneto-thermal and dielectric properties of biferroic YCrO{sub 3} prepared by combustion synthesis