Rare earth doped LiYbF{sub 4} phosphors with controlled morphologies: Hydrothermal synthesis and luminescent properties
- State Key Laboratory of Materials-Orient Chemical Engineering, College of Materials Science and Engineering, Nanjing University of Technology, Nanjing 210009 (China)
Highlights: ► LiYbF{sub 4} microparticles as an excellent upconverting materials. ► High temperature and long time can favor high crystalline LiYbF{sub 4} microparticles. ► The shape of LiYbF{sub 4} microparticles can be tuned by the molar ratio of EDTA to Yb{sup 3+}. ► Bright green emission can be obtained by changing the doping concentration of Er{sup 3+}. -- Abstract: High quality monodisperse LiYbF{sub 4} microparticles with shape of octahedron had been prepared via a facile hydrothermal route. The crystalline phase, size, morphology and luminescence properties were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), photoluminescence (PL) spectra and Commission Internationale de L’Eclairage (CIE 1931) chromaticity coordinates, respectively. The influences of reaction temperature, reaction time and the molar ratio of EDTA to Yb{sup 3+} on the crystal phases and shapes of as-prepared products had been investigated in detail. The upconversion (UC) luminescence properties of LiYb{sub 1−x}F{sub 4}:xEr{sup 3+} (x =0.1, 0.2, 0.5, 1, 2, 5 and 10 mol%) particles with octahedral microstructures were studied under 976 nm excitation. The results showed that the luminescence colors of the corresponding products could be tuned to bright green by changing the doping concentration of Er{sup 3+} ion. The luminescence mechanisms for the doped Er{sup 3+} ion were thoroughly analyzed, showing great potential in applications such as biolabels, displays and other optical technologies.
- OSTI ID:
- 22215096
- Journal Information:
- Materials Research Bulletin, Vol. 47, Issue 6; Other Information: Copyright (c) 2012 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
Vacuum ultraviolet and near-infrared excited luminescence properties of Ca{sub 3}(PO{sub 4}){sub 2}:RE{sup 3+}, Na{sup +} (RE=Tb, Yb, Er, Tm, and Ho)
Multimodal emissions from Tb{sup 3+}/Yb{sup 3+} co-doped lithium borate glass: Upconversion, downshifting and quantum cutting