Development of mixed conducting dense nickel/Ca-doped lanthanum zirconate cermet for gas separation application
- CSIR - Central Glass and Ceramic Research Institute, 196 Raja S. C. Mullick Road, Kolkata - 700 032 (India)
- Department of Chemical Technology, Calcutta University, 92 A. P. C. Road, Kolkata - 700 009 (India)
Highlights: Black-Right-Pointing-Pointer Phase pure La{sub 1.95}Ca{sub 0.05}Zr{sub 2}O{sub 7-{delta}} (LCZ) material is prepared by combustion synthesis. Black-Right-Pointing-Pointer LCZ and Ni-LCZ bulk samples are prepared with theoretical density close to 100%. Black-Right-Pointing-Pointer Bulk electrical conductivity {approx}400 S/cm is obtained for Ni-LCZ cermet at 750 Degree-Sign C. -- Abstract: La{sub 1.95}Ca{sub 0.05}Zr{sub 2}O{sub 7-{delta}} (LCZ) and Ni-LCZ cermet have been prepared by combustion synthesis and conventional solid state mixing methods respectively. Both the materials are sintered in air and controlled atmosphere (5% H{sub 2} in Ar). The density obtained for the material sintered at 1400 Degree-Sign C in controlled atmosphere is found to be more than 99.5%. This sintering temperature (1400 Degree-Sign C) is considered to be much lower compared to the conventional sintering temperature. The corresponding total conductivity for such Ni-LCZ cermet materials is {approx}400 S/cm measured at 750 Degree-Sign C having 40 vol% of Ni and 60 vol% LCZ.
- OSTI ID:
- 22212483
- Journal Information:
- Materials Research Bulletin, Vol. 47, Issue 3; Other Information: Copyright (c) 2011 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
Low-temperature synthesis of Li{sub 7}La{sub 3}Zr{sub 2}O{sub 12} with cubic garnet-type structure
High surface area neodymium phosphate nano particles by modified aqueous sol-gel method