Nanocrystalline sol-gel TiO{sub 2}-SnO{sub 2} coatings: Preparation, characterization and photo-catalytic performance
- Department of Materials Engineering, Faculty of Engineering, Tarbiat Modares University, P.O. Box 14115-143, Tehran (Iran, Islamic Republic of)
Highlights: Black-Right-Pointing-Pointer SnO{sub 2} additive enhanced significantly photo-catalytic properties of TiO{sub 2} based thin film for remove of organic compounds. Black-Right-Pointing-Pointer Structural and optical properties are dependent on dopant concentration. Black-Right-Pointing-Pointer TiO{sub 2}-SnO{sub 2} nanocrystalline thin film is promising for photocatalytic properties in visible light. -- Abstract: In this study, preparation of SnO{sub 2} (0-30 mol% SnO{sub 2})-TiO{sub 2} dip-coated thin films on glazed porcelain substrates via sol-gel process has been investigated. The effects of SnO{sub 2} on the structural, optical, and photo-catalytic properties of applied thin films have been studied by X-ray diffraction, Raman spectroscopy, and scanning electron microscopy. Surface topography and surface chemical state of thin films were examined by atomic force microscopy and X-ray photoelectron spectroscopy. XRD patterns showed an increase in peak intensities of the rutile crystalline phase by increasing the SnO{sub 2} content. The prepared Sn doped TiO{sub 2} photo-catalyst films showed optical absorption in the visible light area exhibited excellent photo-catalytic ability for the degradation of methylene blue under visible light irradiation. Best photo-catalytic activity of Sn doped TiO{sub 2} thin films was measured in the TiO{sub 2}-15 mol% SnO{sub 2} sample by the Sn{sup 4+} dopants presented substitution Ti{sup 4+} into the lattice of TiO{sub 2} increasing the surface oxygen vacancies and the surface hydroxyl groups.
- OSTI ID:
- 22212424
- Journal Information:
- Materials Research Bulletin, Vol. 47, Issue 2; Other Information: Copyright (c) 2011 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
Sn-doped polyhedral In{sub 2}O{sub 3} particles: Synthesis, characterization, and origins of luminous emission in wide visible range
Photocatalytic activity of erbium-doped TiO{sub 2} nanoparticles immobilized in macro-porous silica films
Related Subjects
ORGANIC
PHYSICAL AND ANALYTICAL CHEMISTRY
77 NANOSCIENCE AND NANOTECHNOLOGY
ATOMIC FORCE MICROSCOPY
CRYSTALS
DOPED MATERIALS
GLAZES
IRRADIATION
METHYLENE BLUE
NANOSTRUCTURES
OPTICAL PROPERTIES
RAMAN SPECTROSCOPY
RUTILE
SCANNING ELECTRON MICROSCOPY
SURFACES
THIN FILMS
TIN IONS
TIN OXIDES
TITANIUM OXIDES
X-RAY DIFFRACTION
X-RAY PHOTOELECTRON SPECTROSCOPY