Synthesis and photocatalytic activity of mesoporous cerium doped TiO{sub 2} as visible light sensitive photocatalyst

Journal Article · Wed Feb 15 04:00:00 EST 2012 · Materials Research Bulletin

DOI:https://doi.org/10.1016/J.MATERRESBULL.2011.11.049· OSTI ID:22212399

Aman, Noor ^[1]; Satapathy, P. K. ^[2]; Mahato, M. ^[1]; Das, N. N. ^[2]

---

1. CSE Division, CSIR-National Metallurgical Laboratory, Jamshedpur 831007 (India)
2. PG Department of Chemistry, North Orissa University, Baripada 757003, Orissa (India)

Graphical abstract: Cerium doped titania having optimum 5 wt% of cerium can decompose methylene blue and reduce selenium (IV) efficiently under visible light. Highlights: Black-Right-Pointing-Pointer Effect of cerium doping on the surface properties and visible light mediated photocatalytic reaction is studied. Black-Right-Pointing-Pointer Cerium doping increases the anatase phase stability, surface area (up to 137 m{sup 2}/g) and visible light absorption. Black-Right-Pointing-Pointer Importance of Ce{sup 3+}/Ce{sup 4+}, oxygen vacancy, surface area and crystallinity is correlated with improved catalytic activity. Black-Right-Pointing-Pointer Material with 5 wt% Ce is found to be most active photocatalyst for methylene blue decomposition and Se (IV) reduction. -- Abstract: Cerium doped titania materials were synthesized varying the cerium concentration from 0 to 10 wt%. Materials are characterised by XRD, TEM, XPS and N{sub 2} adsorption desorption method. Surface area and visible light absorption substantially increases and crystallite size decreases with the increasing cerium content. Cerium doping stabilizes the anatase phase and surface area even at 600 Degree-Sign C calcination. Photocatalytic activity towards methylene blue decomposition and selenium (IV) reduction is found to increase with the cerium content up to 5 wt% and then decreases. Materials calcined at 600 Degree-Sign C shows better activity than that calcined at 400 Degree-Sign C, even though surface area decreases. Anatase crystallinity mostly decides the photocatalytic activity rather than only surface area. It can be concluded that the optimum visible light absorption and oxygen vacancy with 5% cerium doping enhances the photocatalytic activity. In addition photocatalytic performance is found to depend on the presence of Ce{sup 4+}/Ce{sup 3+} rather than only visible light absorption.

• OSTI ID: 22212399
• Journal Information: Materials Research Bulletin, Journal Name: Materials Research Bulletin Journal Issue: 2 Vol. 47; ISSN MRBUAC; ISSN 0025-5408
• Country of Publication: United States
• Language: English

Related Subjects

36 MATERIALS SCIENCE
37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CHEMISTRY
ABSORPTION
ADSORPTION
CERIUM
CERIUM IONS
DESORPTION
DOPED MATERIALS
METHYLENE BLUE
NANOSTRUCTURES
PHOTOCATALYSIS
SURFACE AREA
TITANIUM OXIDES
TRANSMISSION ELECTRON MICROSCOPY
X-RAY DIFFRACTION
X-RAY PHOTOELECTRON SPECTROSCOPY