Solvothermal synthesis of SrMoO{sub 4}:Ln (Ln = Eu{sup 3+}, Tb{sup 3+}, Dy{sup 3+}) nanoparticles and its photoluminescence properties at room temperature
- College of Material Science and Chemical Engineering, Harbin Engineering University, Harbin 150001 (China)
- State Key Laboratory of Rare Earth Resource Utilization, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022 (China)
Research highlights: {yields} A facile hydrothermal process was used to fabricate luminescent nanocrystals. {yields} The PL emissions the nanocrystals can be tuned by doping different rare-earth ions. {yields} A possible formation scheme for the as-synthesized nanocrystals was presented. -- Abstract: Rare-earth ions (Eu{sup 3+}, Tb{sup 3+}, Dy{sup 3+}) doped SrMoO{sub 4} nanoparticles were prepared by solvothermal route using oleic acid as surfactant to control the particle shape and size. X-ray diffraction (XRD), transmission electron microscopy (TEM), X-ray photoelectron spectra (XPS), photoluminescence spectra (PL) and the kinetic decay times were applied to characterize the obtained samples. The XRD patterns reveal that all the doped samples are assigned to the scheelite-type tetragonal structure of SrMoO{sub 4} phase. In addition, the as-synthesized SrMoO{sub 4}:Ln (Ln = Eu{sup 3+}, Tb{sup 3+}, Dy{sup 3+}) particles are high purity well crystallized and with the average size of 30-50 nm. The possible formation process of SrMoO{sub 4}:Ln (Ln = Eu{sup 3+}, Tb{sup 3+}, Dy{sup 3+}) nanoparticles have been discussed as well. Upon excitation by ultraviolet radiation, the as-synthesized SrMoO{sub 4}:Ln (Ln = Eu{sup 3+}, Tb{sup 3+}, Dy{sup 3+}) nanoparticles exhibit the characteristic emission lines of corresponding Eu{sup 3+}, Tb{sup 3+}, Dy{sup 3+}, respectively.
- OSTI ID:
- 22210011
- Journal Information:
- Materials Research Bulletin, Vol. 46, Issue 3; Other Information: Copyright (c) 2010 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
Solvothermal synthesis and luminescent properties of monodisperse LaPO{sub 4}:Ln (Ln=Eu{sup 3+}, Ce{sup 3+}, Tb{sup 3+}) particles
Synthesis and characterization of monodisperse spherical SiO{sub 2}-RE{sub 2}O{sub 3} (RE=rare earth elements) and SiO{sub 2}-Gd{sub 2}O{sub 3}:Ln{sup 3+} (Ln=Eu, Tb, Dy, Sm, Er, Ho) particles with core-shell structure
Related Subjects
ORGANIC
PHYSICAL AND ANALYTICAL CHEMISTRY
77 NANOSCIENCE AND NANOTECHNOLOGY
CONTROL
DYSPROSIUM IONS
EUROPIUM IONS
EXCITATION
NANOSTRUCTURES
OLEIC ACID
PARTICLES
PHOTOLUMINESCENCE
RARE EARTHS
SPECTRA
SYNTHESIS
TERBIUM IONS
TRANSMISSION ELECTRON MICROSCOPY
X-RAY DIFFRACTION
X-RAY PHOTOELECTRON SPECTROSCOPY