Modified Pechini synthesis of tricalcium aluminate powder
Tricalcium aluminate (Ca{sub 3}Al{sub 2}O{sub 6}-C{sub 3}A) was obtained by a modified Pechini synthesis in order to eliminate successive thermal treatments and intermediate grinding usually performed between the two sintering steps and in order to reduce the sintering temperature. Our results indicated that pure C{sub 3}A was obtained, by a single step thermal treatment at 1300 Degree-Sign C for 4 h and 1350 Degree-Sign C for 1 h. The synthesis was confirmed by XRD, FT-IR and free lime analyses. The morphology of synthesised C{sub 3}A was assessed by electron microscopy (SEM and TEM, HRTEM) and it was observed a high tendency of the particles to form aggregates and the individual particles seem to be single crystals. The bioactivity was assessed by specimen soaking in simulated body fluid (SBF) for 7 days; the hydrate (i.e. 3CaO Bullet-Operator Al{sub 2}O{sub 3} Bullet-Operator 6H{sub 2}O formed at the C{sub 3}A surface), can act as nucleation centers for the resulted phosphate phases. - Highlights: Black-Right-Pointing-Pointer A modified Pechini synthesis was used for obtained of tricalcium aluminate. Black-Right-Pointing-Pointer C{sub 3}A was obtained at 1300 Degree-Sign C/4 h and 1350 Degree-Sign C/1 h. Black-Right-Pointing-Pointer Were eliminated successive thermal treatments and intermediate grinding. Black-Right-Pointing-Pointer The morphology of synthesised C{sub 3}A was assessed by electron microscopy (SEM, TEM). Black-Right-Pointing-Pointer Was observed a high tendency of the particles to form aggregates.
- OSTI ID:
- 22163147
- Journal Information:
- Materials Characterization, Journal Name: Materials Characterization Journal Issue: Complete Vol. 73; ISSN 1044-5803; ISSN MACHEX
- Country of Publication:
- United States
- Language:
- English
Similar Records
Chromium incorporation into TiO{sub 2} at high pressure
Power factor improvement in hydrothermally synthesized Bi{sub 2-x}Sb{sub x}Te{sub 3} (x=1.5) - carbon sphere composites