Size effects of primary/secondary twins on the atomistic deformation mechanisms in hierarchically nanotwinned metals
- State Key Laboratory of Nonlinear Mechanics, Institute of Mechanics, Chinese Academy of Science, Beijing 100190 (China)
A series of large-scale molecular dynamics simulations have been performed to investigate the tensile properties of nanotwinned (NT) copper with hierarchically twinned structures (HTS). For the same grain size d and the same spacing of primary twins {lambda}{sub 1}, the average flow stress first increases as the spacing of secondary twins {lambda}{sub 2} decreases, reaching a maximum at a critical {lambda}{sub 2}, and then decreases as {lambda}{sub 2} becomes even smaller. The smaller the spacing for {lambda}{sub 1}, the smaller the critical spacing for {lambda}{sub 2}. There exists a transition in dominating deformation mechanisms, occurring at a critical spacing of {lambda}{sub 2} for which strength is maximized. Above the critical spacing of {lambda}{sub 2}, the deformation mechanisms are dominated by the two Hall-Petch type strengthening mechanisms: (a) partial dislocations emitted from grain boundaries (GBs) travel across other GBs and twin boundaries (TBs); (b) partial dislocations emitted from TBs travel across other TBs. Below the critical spacing of {lambda}{sub 2}, the deformation mechanism is dominated by the two softening mechanisms: (a) Partial dislocations emitted from boundaries of the primary twins travel parallel to the TBs of the secondary twins, leading to detwinning of the secondary twins; (b) Boundaries of the primary twins shift entirely, leading to thickening in one part of primary twins and thinning in the other part of primary twins. The present results should provide insights to design the microstructures for reinforcing the mechanical properties in the NT metals with HTS.
- OSTI ID:
- 22162977
- Journal Information:
- Journal of Applied Physics, Vol. 113, Issue 20; Other Information: (c) 2013 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0021-8979
- Country of Publication:
- United States
- Language:
- English
Similar Records
Columnar Grain-driven Plasticity and Cracking in Nanotwinned FCC Metals
Quantitative insights into the dislocation source behavior of twin boundaries suggest a new dislocation source mechanism