Mesoporous TiO{sub 2} aggregate photoanode with high specific surface area and strong light scattering for dye-sensitized solar cells
- Key Laboratory for Renewable Energy, Chinese Academy of Sciences, Beijing Key Laboratory for New Energy Materials and Devices, Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, Chinese Academy of Sciences, Beijing 100190 (China)
- Center for Materials Crystallography, Department of Chemistry and Interdisciplinary Nanoscience Center, Aarhus University, DK-8000 Aarhus (Denmark)
Phase-pure anatase TiO{sub 2} nanocrystallite aggregates synthesized by a continuous supercritical fluid process have been first used for fabricating mesoporous photoanodes of dye-sensitized solar cells (DSCs). Due to the small size (11 nm) of the TiO{sub 2} nanocrystallites in the aggregates, the mesoporous photoanode provides a high specific surface area, 80 m{sup 2}/g, which ensures high dye loading. At the same time, the submicrometer-sized aggregates endow the mesoporous photoanode with strong light scattering effect. Therefore, the light harvesting efficiency of the photoanode is increased. With an improved short-circuit current density, a high overall power conversion efficiency of 8.65% (100 mW/cm{sup 2}, AM 1.5) is achieved without additional scattering layers, 12% enhanced compared with the DSCs fabricated from commercial Degussa P25 with exactly the same procedures. In addition, this supercritical fluid process is scalable and rapid (less than one minute) for TiO{sub 2} aggregates synthesis, which will push the commercialization of DSCs in the future. - Graphical abstract: Due to the special morphology and structure, the photoanode of DSCs provides high specific surface area and strong light scattering at the same time, which results in high conversion efficiencies of the DSCs. Table of contents: Thanks to the synchronous realization of high specific surface area and strong light scattering, a high efficiency of 8.65% was achieved based on a novel mesoporous TiO{sub 2} aggregates photoanode for DSCs. Highlights: Black-Right-Pointing-Pointer The TiO{sub 2} aggregate photoanode provides a possible route for highly efficient DSCs. Black-Right-Pointing-Pointer Photoanode with high dye loading and light scattering is successfully fabricated. Black-Right-Pointing-Pointer TiO{sub 2} synthesized by a supercritical fluid process is first applied to DSCs. Black-Right-Pointing-Pointer The synthesis method and high efficiency will push the commercialization of DSCs.
- OSTI ID:
- 22149975
- Journal Information:
- Journal of Solid State Chemistry, Vol. 196; Other Information: Copyright (c) 2012 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
P25 niblet-like coated on large void space TiO{sub 2} nanotubes arrays for high-rate charge-collection and improved photoconversion efficiency
Enhanced performance of dye-sensitized solar cells based on TiO{sub 2} with NIR-absorption and visible upconversion luminescence