4f and 5d energy levels of the divalent and trivalent lanthanide ions in M{sub 2}Si{sub 5}N{sub 8} (M=Ca, Sr, Ba)
- Luminescent Materials Research Group, Faculty of Applied Sciences, Delft University of Technology, Mekelweg 15, 2629JB Delft (Netherlands)
- Energy Materials and Devices, Department of Chemical Engineering and Chemistry, Eindhoven University of Technology, Den Dolech 2, 5600MB Eindhoven (Netherlands)
Optical data of Sm, Tb and Yb doped Ca{sub 2}Si{sub 5}N{sub 8} and Sr{sub 2}Si{sub 5}N{sub 8} phosphors that have been prepared by solid-state synthesis, are presented. Together with luminescence data from literature on Ce{sup 3+} and Eu{sup 2+} doping in the M{sub 2}Si{sub 5}N{sub 8} (M=Ca, Sr, Ba) hosts, energy level schemes were constructed showing the energy of the 4f and 5d levels of all divalent and trivalent lanthanide ions relative to the valence and conduction band. The schemes were of great help in interpreting the optical data of the lanthanide doped phosphors and allow commenting on the valence stability of the ions, as well as the stability against thermal quenching of the Eu{sup 2+}d-f emission. Tb{sup 3+} substitutes on both a high energy and a low energy site in Ca{sub 2}Si{sub 5}N{sub 8}, due to which excitation at 4.77 eV led to emission from both the {sup 5}D{sub 3} and {sup 5}D{sub 4} levels, while excitation at 4.34 eV gave rise to mainly {sup 5}D{sub 4} emission. Doping with Sm resulted in typical Sm{sup 3+}f-f line absorption, as well as an absorption band around 4.1 eV in Ca{sub 2}Si{sub 5}N{sub 8} and 3.6 eV in Sr{sub 2}Si{sub 5}N{sub 8} that could be identified as the Sm{sup 3+} charge transfer band. Yb on the other hand was incorporated in both the divalent and the trivalent state in Ca{sub 2}Si{sub 5}N{sub 8}. - Graphical abstract: Energy level schemes showing the 4f ground states of the trivalent ( Black-Down-Pointing-Small-Triangle ) and divalent ( Black-Up-Pointing-Small-Triangle ) lanthanide ions and lowest energy 5d states of the trivalent ({nabla}) and divalent ({Delta}) ions with respect to the valence and conduction bands of Ca{sub 2}Si{sub 5}N{sub 8} (left) and Sr{sub 2}Si{sub 5}N{sub 8} (right). Highlights: Black-Right-Pointing-Pointer Construction of energy level schemes of all lanthanides within the M{sub 2}Si{sub 5}N{sub 8} hosts. Black-Right-Pointing-Pointer Construction was done by analyzing existing as well as new spectroscopic data. Black-Right-Pointing-Pointer Tb{sup 3+}d-f emission from two different Ca sites in Ca{sub 2}Si{sub 5}N{sub 8} has been observed. Black-Right-Pointing-Pointer Observation of the Sm{sup 3+} charge transfer band in Ca{sub 2}Si{sub 5}N{sub 8} and Sr{sub 2}Si{sub 5}N{sub 8}. Black-Right-Pointing-Pointer Ytterbium has been found in the divalent and trivalent state in Ca{sub 2}Si{sub 5}N{sub 8}.
- OSTI ID:
- 22131179
- Journal Information:
- Journal of Solid State Chemistry, Vol. 197; Other Information: Copyright (c) 2012 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
Electronic structure of rare-earth chromium antimonides RECrSb{sub 3} (RE=La-Nd, Sm, Gd-Dy, Yb) by X-ray photoelectron spectroscopy
Solvothermal synthesis of a bimetallic thiometallate containing germanium in two oxidation states