Rietveld refinement and ionic conductivity of Ca{sub 8.4}Bi{sub 1.6}(PO{sub 4}){sub 6}O{sub 1.8}
- Laboratory of the Physics of Materials, Faculty of Science of Bizerte, University of Carthage, Zarzouna 7021, Bizerte (Tunisia)
- LdoF-UMR 6010, Faculty of Science and Techniques, University of Maine, Avenue O. Messiaen, 7285 Le Mans Cedex 9 (France)
- Laboratory of the Physico-Chemistry of Solid States, LR11 ES51, University of Sfax, Road of Soukra km 4, Sfax 3038 (Tunisia)
The structure of Ca{sub 8.4}Bi{sub 1.6}(PO{sub 4}){sub 6}O{sub 1.8}, isostructural with Fluoroapatite, was determined by X-ray powder diffraction methods. The results of Rietveld refinement revealed that the formula of this compound is [Ca{sub 4}]{sup 4f}[Ca{sub 4.4}Bi{sub 1.6}]{sup 6h}(PO{sub 4}){sub 6}[O{sub 1.8}]{sup 2a}, space group P63/m (a=9.468 (3) A, c=6.957 (3) A). A total substitution of Bi{sup 3+} ions in the (6h) sites was related particularly to the high polarizability of the Bi{sup 3+} ion compared to Ca{sup 2+}. The observed frequencies in the Raman and infrared spectra were explained and discussed on the basis of unit-cell group analyses and in comparison with Fluoroapatite and other oxyapatites. The ionic conductivity over a wide range of temperature was investigated according to the complex impedance method. The highest overall conductivity values were found at {sigma}{sub 700 Degree-Sign C} =5.03 Multiplication-Sign 10{sup -7} S cm{sup -1} and E{sub a}=0.50 eV. - Graphical abstract: The final Rietveld refinement plot of the Ca{sub 8.4}Bi{sub 1.6} (PO{sub 4}){sub 6}O{sub 1.8}. Highlights: Black-Right-Pointing-Pointer The Rietveld refinement revealed that the formula of this compound is Ca{sub 8.4}Bi{sub 1.6}(PO{sub 4}){sub 6}O{sub 1.8}. Black-Right-Pointing-Pointer Vibrational spectroscopy supports the high symmetry P63/m space group for this apatite. Black-Right-Pointing-Pointer This apatite contained channels where oxygen ions were located in 2a sites. Black-Right-Pointing-Pointer The possibility of anionic conduction along these channels was considered.
- OSTI ID:
- 22131170
- Journal Information:
- Journal of Solid State Chemistry, Vol. 197; Other Information: Copyright (c) 2012 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
Quadruple-layered perovskite (CuCl)Ca{sub 2}NaNb{sub 4}O{sub 13}
Crystal structure and stoichiometry of the Ca/sub 2+x/Nd/sub 8-x/(SiO/sub 4/)/sub 6/O/sub 2-1/2x/ system