Titanate nanotube thin films with enhanced thermal stability and high-transparency prepared from additive-free sols
- Supramolecular and Nanostructured Materials Research Group of the Hungarian Academy of Sciences, University of Szeged, Aradi vertanuk tere 1, H-6720 Szeged (Hungary)
- Department of Physical Chemistry and Materials Science, University of Szeged, Aradi vertanuk tere 1, H-6720 Szeged (Hungary)
- Institute for Technical Physics and Materials Science MFA, Research Center for Natural Sciences, Konkoly-Thege ut 29-33, H-1121 Budapest (Hungary)
Titanate nanotubes were synthesized from TiO{sub 2} in alkaline medium by a conventional hydrothermal method (150 Degree-Sign C, 4.7 bar). To obtain hydrogen titanates, the as-prepared sodium titanates were treated with either HCl or H{sub 3}PO{sub 4} aqueous solutions. A simple synthesis procedure was devised for stable titanate nanotube sols without using any additives. These highly stable ethanolic sols can readily be used to prepare transparent titanate nanotube thin films of high quality. The resulting samples were studied by X-ray diffraction, N{sub 2}-sorption measurements, Raman spectroscopy, transmission and scanning electron microscopy, X-ray photoelectron spectroscopy and spectroscopic ellipsometry. The comparative results of using two kinds of acids shed light on the superior thermal stability of the H{sub 3}PO{sub 4}-treated titanate nanotubes (P-TNTs). X-ray photoelectron spectroscopy revealed that P-TNTs contains P in the near-surface region and the thermal stability was enhanced even at a low ({approx}0.5 at%) concentration of P. After calcination at 500 Degree-Sign C, the specific surface areas of the HCl- and H{sub 3}PO{sub 4}-treated samples were 153 and 244 m{sup 2} g{sup -1}, respectively. The effects of H{sub 3}PO{sub 4} treatment on the structure, morphology and porosity of titanate nanotubes are discussed. - Graphical Abstract: TEM picture (left) shows P-TNTs with diameters about 5-6 nm. Inset shows a stable titanate nanotube sol illuminated by a 532 nm laser beam. Due to the presence of the nanoparticles the way of the light is visible in the sol. Cross sectional SEM picture (right) as well as ellipsometry revealed the formation of optical quality P-TNT films with thicknesses below 50 nm. Highlights: Black-Right-Pointing-Pointer H{sub 3}PO{sub 4} treatment led to TNTs with high surface area even after calcination at 500 Degree-Sign C. Black-Right-Pointing-Pointer H{sub 3}PO{sub 4}-treated TNTs preserved their nanotube morphology up to 500 Degree-Sign C. Black-Right-Pointing-Pointer Stable TNT sols can be prepared by the peptization of TNT gels. Black-Right-Pointing-Pointer High-transparency TNT thin films of high quality were fabricated.
- OSTI ID:
- 22131141
- Journal Information:
- Journal of Solid State Chemistry, Vol. 192; Other Information: Copyright (c) 2012 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
Preparation and photocatalytic activity for water splitting of Pt-Na{sub 2}Ta{sub 2}O{sub 6} nanotube arrays
Vapor-phase synthesis of a solid precursor for {alpha}-alumina through a catalytic decomposition of aluminum triisopropoxide
Related Subjects
ORGANIC
PHYSICAL AND ANALYTICAL CHEMISTRY
77 NANOSCIENCE AND NANOTECHNOLOGY
CALCINATION
HYDROCHLORIC ACID
HYDROTHERMAL SYNTHESIS
NANOTUBES
PHOSPHORIC ACID
RAMAN SPECTROSCOPY
SCANNING ELECTRON MICROSCOPY
SOLS
STABILITY
THIN FILMS
TITANATES
TITANIUM OXIDES
VISIBLE RADIATION
X-RAY DIFFRACTION
X-RAY PHOTOELECTRON SPECTROSCOPY