Crystal structure and thermoelectric properties of clathrate, Ba{sub 8}Ni{sub 3.5}Si{sub 42.0}: Small cage volume and large disorder of the guest atom
- Department of Chemistry, University of California, One Shields Ave., Davis, CA 95616 (United States)
- Thermal Energy Conversion Technologies Group, Jet Propulsion Laboratory/California Institute of Technology, Pasadena, CA 91109 (United States)
Samples with the type-I clathrate composition Ba{sub 8}Ni{sub x}Si{sub 46-x} have been synthesized and their structure and thermoelectric properties characterized. Microprobe analysis indicates the Ni incorporation to be 2.62{<=}x{<=}3.53. The x=3.5 phase crystallizes in the type-I clathrate structure (space group: Pm-3n) with a lattice parameter of 10.2813(3) A. The refined composition was Ba{sub 8}Ni{sub 3.5}Si{sub 42.0}, with small vacancies, 0.4 and 0.5 atoms per formula unit, at the 2a and 6c sites, respectively. The position of the Ba2 atom in the large cage was modeled using a 4-fold split position (24j site), displaced 0.18 A from the cage center (6d site). The volume of the large cage is calculated to be 146 A{sup 3}, smaller than other clathrates with similar cation displacement. The sample shows n-type behavior with a maximum of -50 {mu}V/K at 823 K above which the Seebeck coefficient decreases, suggesting mixed carriers. Lattice thermal conductivity, {kappa}{sub l}, is 55 mW/K above 600 K. - Graphical abstract: Seebeck coefficient and resistivity of the type-I clathrate Ba{sub 8}Ni{sub 3.5}Si{sub 41.0}. Structure show's large displacement of the Ba cation in the large cage (6c site). Highlights: Black-Right-Pointing-Pointer Crystal structure of the Ba{sub 8}Ni{sub 3.5}Si{sub 41.0} reported. Black-Right-Pointing-Pointer Vacancies at the 2a and 6c sites. Black-Right-Pointing-Pointer Large disorder of Ba guest atom, 0.18 A from cage center. Black-Right-Pointing-Pointer Structure is compared to Ba{sub 8}Si{sub 46} and other type-I clathrates. Black-Right-Pointing-Pointer Max Seebeck of -50.7 {mu}V/C at 798.4 K, thermal conductivity {approx}55 mW/K.
- OSTI ID:
- 22131107
- Journal Information:
- Journal of Solid State Chemistry, Vol. 192; Other Information: Copyright (c) 2012 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
Electronic and transport properties of polycrystalline Ba{sub 8}Ga{sub 15}Ge{sub 31} type I clathrate prepared by SPS method
Liquidus projection of the Ag-Ba-Ge system and melting points of clathrate type-I compounds