Phonon spectrum and interaction between nanotubes in single-walled carbon nanotube bundles at high pressures and temperatures
The Raman spectra of single-walled carbon nanotubes at temperatures up to 730 K and pressures up to 7 GPa have been measured. The behavior of phonon modes and the interaction between nanotubes in bundles have been studied. It has been found that the temperature shift of the vibrational G mode is completely reversible, whereas the temperature shift of radial breathing modes is partially irreversible and the softening of the modes and narrowing of phonon bands are observed. The temperature shift and softening of radial breathing modes are also observed when samples are irradiated by laser radiation with a power density of 6.5 kW/mm{sup 2}. The dependence of the relative frequency {Omega}/{Omega}{sub 0} for G{sup +} and G{sup -} phonon modes on the relative change A{sub 0}/A in the triangular lattice constant of bundles of nanotubes calculated using the thermal expansion coefficient and compressibility coefficient of nanotube bundles shows that the temperature shift of the G mode is determined by the softening of the C-C bond in nanotubes. An increase in the equilibrium distances between nanotubes at the breaking of random covalent C-C bonds between nanotubes in bundles of nanotubes is in my opinion the main reason for the softening of the radial breathing modes.
- OSTI ID:
- 22069232
- Journal Information:
- Journal of Experimental and Theoretical Physics, Journal Name: Journal of Experimental and Theoretical Physics Journal Issue: 6 Vol. 115; ISSN JTPHES; ISSN 1063-7761
- Country of Publication:
- United States
- Language:
- English
Similar Records
Raman spectroscopy of single-wall carbon nanotubes and graphite irradiated by {gamma} rays
Effect of residual catalyst on the vibrational modes of single-walled carbon nanotubes