C-Cr segregation at grain boundary before the carbide nucleation in Alloy 690
- Institute of Materials, Shanghai University, Shanghai, 200072 (China)
- Laboratory for Microstructures, Shanghai University, Shanghai, 200444 (China)
The grain boundary segregation in Alloy 690 was investigated by atom probe tomography. B, C and Si segregated at the grain boundary. The high concentration regions for each segregation element form a set of straight arrays that are parallel to each other in the grain boundary plane. The concentration fluctuation has a periodicity of about 7 nm in the grain boundary plane. Before the Cr{sub 23}C{sub 6} nucleation at grain boundaries, the C-Cr co-segregate on one side of the grain boundaries while not the exact grain boundary core regions have been detected. The reasons why grain boundary carbides have coherent orientation relationship only with one side of nearby grain which grain boundary is located at high index crystal plane were discussed. - Highlights: Black-Right-Pointing-Pointer Grain boundary segregation in Alloy 690 was investigated by atom probe tomography. Black-Right-Pointing-Pointer B, C and Si segregate at the grain boundary. Black-Right-Pointing-Pointer Concentration of segregated atoms periodicity fluctuated in the grain boundary plane. Black-Right-Pointing-Pointer C and Cr co-segregate on one side of the grain boundary before carbide nucleation.
- OSTI ID:
- 22066438
- Journal Information:
- Materials Characterization, Vol. 66, Issue Complete; Other Information: Copyright (c) 2012 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 1044-5803
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effect of carbon content on solidification behaviors and morphological characteristics of the constituent phases in Cr-Fe-C alloys
Characterization of SCC Initiation Precursors in Cold-Worked Alloy 690