Rolling contact fatigue in high vacuum using ion plated nickel-copper-silver solid lubrication
- Mechanical Engineering Department, University of Wisconsin-Milwaukee, Milwaukee, Wisconsin 53211-3029 (United States)
Ion plated, nickel-copper-silver coated steel ball bearings that were tested in rolling contact fatigue (RCF) experiments in high vacuum are presented in this article. ANSI T5 ball bearings were coated with approximately 10 nm of nickel-copper followed by 100 nm of silver using a dc ion plating process. The balls were then tested for RCF in vacuum in the 10{sup -7} Torr range at 130 Hz rotational speed and at 4.1 GPa Hertzian contact stress. The significance of this work is in the extension of RCF testing to an ultrahigh vacuum (UHV) application using silver as a lubricant instead of oil. The effects of pressure and voltage on the ion plating process were also investigated using scanning electron microscopy and RCF life testing in UHV. Test results with a ball size of 5/16 in. in UHV show that deposition at voltages greater than 2.5 kV shortens the RCF life and introduces a unique failure mode. Voltage and pressure fluctuations during the deposition process result in significant thickness monitor measurement errors as well. A regulator control scheme that minimizes the process pressure overshoot is also simulated.
- OSTI ID:
- 22054011
- Journal Information:
- Journal of Vacuum Science and Technology. A, International Journal Devoted to Vacuum, Surfaces, and Films, Journal Name: Journal of Vacuum Science and Technology. A, International Journal Devoted to Vacuum, Surfaces, and Films Journal Issue: 1 Vol. 29; ISSN 1553-1813
- Country of Publication:
- United States
- Language:
- English
Similar Records
Rolling contact fatigue characteristics of thermal sprayed tungsten carbide coatings
Rolling-contact fatigue and wear of CVD-SiC with residual surface compression