Fatigue degradation in compressively loaded composite laminates. FLD33 ERRCHK FLD04
This report describes an experimental program conducted to assess the effect of imbedded delaminations on the compression fatigue behavior of quasi-isotropic, T300/5208, graphite/epoxy laminates. Teflon imbedments were introduced during panel layup to create delaminations. Test specimens were 64-ply thick, and had 3.81 cm square test sections that were unconstrained laterally during compression testing. Static and constant amplitude (R=10, omega= 10 Hz) fatigue tests were conducted. S-N data and half-life residual strength data were obtained. During static compression loading, the maximum deflection of the buckled delaminated region was recorded. Under compression fatigue, growth of the imbedded delamination was identified as the predominant failure mode in most of the test cases. Specimens that exhibited other failures had a single low stiffness ply above the Teflon imbedment. Delamination growth during fatigue was monitored using DIB- enhanced radiography. In specimens with buried delaminations, the dye-penetrant (DIB) was introduced into the delaminated region through a minute laser-drilled hole, using a hypodermic needle. A low-kV, microfocus, X-ray unit was mounted near the test equipment to efficiently record the cyclic growth of buried delaminations on Polaroid film.
- Research Organization:
- Northrop Corp., Hawthorne, CA (United States). Aircraft Div.
- OSTI ID:
- 220302
- Report Number(s):
- AD-A--301582/3/XAB; NOR--81-79; CNN: Contract NAS1-15956
- Country of Publication:
- United States
- Language:
- English
Similar Records
Response of resin transfer molded (RTM) composites under reversed cyclic loading
Delamination initiation in postbuckled dropped-ply laminates