Nanoscale modulations in (KLa)(CaW)O{sub 6} and (NaLa)(CaW)O{sub 6}
- Department of Materials Science and Engineering, University of Pennsylvania, 3231 Walnut Street, Philadelphia, PA 19104 (United States)
- Materials Science and Technology Division, Oak Ridge National Laboratory, Oak Ridge, TN 37831 (United States)
Complex nanoscale modulations are identified in two new A-site ordered perovskites, (KLa)(CaW)O{sub 6} and (NaLa)(CaW)O{sub 6}. In (KLa)(CaW)O{sub 6}, selected-area electron diffraction (SAED) and high-resolution transmission electron microscopy (HRTEM) show an incommensurate nanocheckerboard modulation with {approx}9.4 Multiplication-Sign 9.4a{sub p} periodicity (a{sub p} Almost-Equal-To 4 A for the cubic perovskite aristotype). For (NaLa)(CaW)O{sub 6} a one-dimensional modulation is observed with a {approx}16(1 1 0)a{sub p} repeat; the Left-Pointing-Angle-Bracket 1 1 0 Right-Pointing-Angle-Bracket orientation of the nanostripes is different from the Left-Pointing-Angle-Bracket 1 0 0 Right-Pointing-Angle-Bracket stripes observed in other mixed A-site systems. Studies using high temperature x-ray diffraction suggest the formation of the complex modulations is associated with small deviations from the ideal 1:1:1:1 stoichiometry of the (A{sup +}La{sup 3+})(CaW)O{sub 6} phases. Z-contrast images acquired on an aberration-corrected microscope provide evidence for deviations from stoichiometry with a {approx}1:15 periodic arrangement of La{sub 4/3}(CaW)O{sub 6}:(NaLa)(CaW)O{sub 6} nano-phases. - Graphical abstract: Complex nanoscale modulations are identified in two new A-site ordered perovskites, (KLa)(CaW)O{sub 6} and (NaLa)(CaW)O{sub 6}. In (KLa)(CaW)O{sub 6}, selected-area electron diffraction and high-resolution transmission electron microscopy show a two-dimensional, nanocheckerboard modulation. For (NaLa)(CaW)O{sub 6} a one-dimensional modulation is observed; the Left-Pointing-Angle-Bracket 1 1 0 Right-Pointing-Angle-Bracket orientation of the nanostripes is different from the Left-Pointing-Angle-Bracket 1 0 0 Right-Pointing-Angle-Bracket stripes observed in other mixed A-site systems. Highlights: Black-Right-Pointing-Pointer Two new A-site ordered perovskites were synthesized, (KLa)(CaW)O{sub 6} and (NaLa)(CaW)O{sub 6}. Black-Right-Pointing-Pointer Unusual 1D and 2D nanoscale patterns were observed. Black-Right-Pointing-Pointer Tolerance factor shown to be not enough to predict the observed morphologies. Black-Right-Pointing-Pointer High temperature x-ray diffraction data suggests a loss of stoichiometry is related to the modulations. Black-Right-Pointing-Pointer Z-contrast imaging provides direct evidence for non-stoichiometry and a new model.
- OSTI ID:
- 22012195
- Journal Information:
- Journal of Solid State Chemistry, Vol. . 191; Other Information: Copyright (c) 2012 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
Double perovskite Sr{sub 2}FeMoO{sub 6-x}N{sub x} (x=0.3, 1.0) oxynitrides with anionic ordering
New nonlinear optical potassium iodate K[IO{sub 3}] and borates K{sub 3}[B{sub 6}O{sub 10}]Br, KTa[B{sub 4}O{sub 6}(OH){sub 4}](OH){sub 2}{center_dot}1.33H{sub 2}O-Synthesis, structures and relation to the properties