K{sub 2}NaOsO{sub 5.5} and K{sub 3}NaOs{sub 2}O{sub 9}: The first osmium perovskites containing alkali cations at the 'A' site
Journal Article
·
· Journal of Solid State Chemistry
- Stuttgart, Max-Planck-Institut fuer Festkoerperforschung, Heisenbergstrasse 1, 70569 Stuttgart (Germany)
K{sub 2}NaOsO{sub 5.5} and K{sub 3}NaOs{sub 2}O{sub 9} were obtained from solid-state reactions of potassium superoxide, sodium peroxide and osmium metal at elevated oxygen pressures. K{sub 2}NaOsO{sub 5.5} crystallizes as an oxygen-deficient cubic double perovskite in space group Fm3{sup Macron }m with a=8.4184(5) A and contains isolated OsO{sub 6} octahedra. K{sub 3}NaOs{sub 2}O{sub 9} crystallizes hexagonally in P6{sub 3}/mmc with a=5.9998(4) A and c=14.3053(14) A. K{sub 3}NaOs{sub 2}O{sub 9} consists of face sharing Os{sub 2}O{sub 9} pairs of octahedra. According to magnetic measurements K{sub 2}NaOsO{sub 5.5} is diamagnetic, whereas K{sub 3}NaOs{sub 2}O{sub 9} displays strong antiferromagnetic coupling (T{sub N}=140 K), indicating enhanced magnetic interactions within the octahedral pair. - Graphical abstract: High oxidation states of Os, obtained by high oxygen pressure synthesis, are accommodated in double and triple perovskite matrices. K{sub 3}NaOs{sub 2}O{sub 9} displays enhanced magnetic interactions. Highlights: Black-Right-Pointing-Pointer New osmates containing highly oxidized Os were obtained by high O{sub 2} pressure synthesis. Black-Right-Pointing-Pointer High oxidation states of Os are accommodated in double and triple perovskite matrices. Black-Right-Pointing-Pointer Both compounds represent the first Os perovskites with an alkali metal at the A site. Black-Right-Pointing-Pointer K{sub 3}NaOs{sub 2}O{sub 9} displays enhanced magnetic interactions within the octahedral pair.
- OSTI ID:
- 22012185
- Journal Information:
- Journal of Solid State Chemistry, Journal Name: Journal of Solid State Chemistry Vol. . 191; ISSN 0022-4596; ISSN JSSCBI
- Country of Publication:
- United States
- Language:
- English
Similar Records
Magnetisation studies of phase co-existence in Gd{sub 1-x}Ca{sub x}BaCo{sub 2}O{sub 5.5}
Physical properties of double perovskite-type barium neodymium osmate Ba{sub 2}NdOsO{sub 6}
A high temperature neutron diffraction study of the double perovskite Ba{sub 2}{sup 154}SmMoO{sub 6}
Journal Article
·
Sun Apr 15 00:00:00 EDT 2012
· Materials Research Bulletin
·
OSTI ID:22212485
Physical properties of double perovskite-type barium neodymium osmate Ba{sub 2}NdOsO{sub 6}
Journal Article
·
Mon Jan 14 23:00:00 EST 2013
· Journal of Solid State Chemistry
·
OSTI ID:22131182
A high temperature neutron diffraction study of the double perovskite Ba{sub 2}{sup 154}SmMoO{sub 6}
Journal Article
·
Fri Dec 14 23:00:00 EST 2012
· Journal of Solid State Chemistry
·
OSTI ID:22149958