Equal Channel Angular Pressing (ECAP) and Its Application to Grain Refinement of Al-Zn-Mg-Cu Alloy
Microstructure of a metal can be considerably changed by severe plastic deformation techniques such as high pressure torsion, extrusion and equal-channel angular pressing (ECAP). Among these methods, ECAP is particularly attractive because it has a potential for introducing significant grain refinement and homogeneous microstructure into bulk materials. Typically, it reduces the grain size to the submicrometer level or even nanometer range and thus produces materials that are capable of exhibiting unusual mechanical properties. In the present study, a test unites for equal channel angular pressing was constructed and this system was used for Al-Zn-Mg-Cu alloy. After the optimization tests, it was seen that the most effective lubricant for the dies was MoS{sub 2}, the pressing pressure was around 25-35 ton and the pressing speed was 2 mm/s. By using these parameters, the Al-Zn-Mg-Cu alloy was successfully ECAPed up to 14 passes at 200 deg. C using route C. After ECAP tests, the specimens were characterized by transmission electron microscope (TEM), hardness and macrostructural investigations. It was seen that the plastic deformation in the ECAPed specimens occurred from edge to the centre like whirlpool. In addition, the deformation intensity increased with increasing pass number. The grain size of the specimens effectively also decreased with increasing pass number. That is, while the grain size of unECAPed specimen was 10 {mu}m, this value decreased to 300 nm after 14 passes. At the beginning, while there was a banding tendency in the grains toward deformation direction, homogeneous and equiaxed grains were formed with increasing pass number. This grain refinement was as a result of an interaction between shear strain and thermal recovery during ECAP processing. Hardness measurements showed that the hardness values increased up to 4 passes, decreased effectively at 6th pass, again increased at 8th pass and after this pass, the hardness again decreased due to dynamic recrystallization.
- OSTI ID:
- 22003958
- Journal Information:
- AIP Conference Proceedings, Journal Name: AIP Conference Proceedings Journal Issue: 1 Vol. 1415; ISSN APCPCS; ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Microstructure characterization of LAE442 magnesium alloy processed by extrusion and ECAP
Evaluation of microstructure anisotropy on room and medium temperature ECAP deformed F138 steel