The aluminum spot weld
- Ford Motor Co., Dearborn, MI (United States). Scientific Lab.
Weld conditions which promote long tip life for aluminum spot welds are not necessarily associated with high weld quality in terms of freedom from defects such as porosity, cracks and expulsion. Schedules which produce good weld nuggets in terms of the peel test and long tip life may not produce a good response in terms of fatigue life. The fatigue life range is optimized by maximizing the weld nugget diameter, i.e., by employing a weld schedule which may lead to expulsion and weld porosity. Weld strength, in both peel and overlap shear configurations, was found to be linearly dependent upon weld diameter. In the peel test, the strength was also dependent upon the base metal thickness, in that for a given thickness, there is a critical diameter for the transition between weld fracture and nugget pull-out. For a given nugget diameter, if pull-out is observed then the strength is greater than if fracture occurs through the weld. In the shear test, the opposite response was observed, the strength for nugget pull-out being less than that for weld shear failure. Weld pull-out was found only for the thinnest base metal thickness tested and the shear load depended only upon the weld diameter over the range of thicknesses tested. Maximum strength in an aluminum spot weld is obtained by maximizing the weld nugget diameter for that thickness of material.
- OSTI ID:
- 218531
- Journal Information:
- Welding Journal, Journal Name: Welding Journal Journal Issue: 3 Vol. 75; ISSN 0043-2296; ISSN WEJUA3
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effects of Failure Modes on Strength of Aluminum Resistance Spot Welds
Effects of Failure Modes on Strength of Aluminum Resistance Spot Welds