Influence of irradiation spectrum and implanted ions on the amorphization of ceramics
Polycrystalline Al2O3, magnesium aluminate spinel (MgAl2O4), MgO, Si3N4, and SiC were irradiated with various ions at 200-450 K, and microstructures were examined following irradiation using cross-section TEM. Amorphization was not observed in any of the irradiated oxide ceramics, despsite damage energy densities up to {similar_to}7 keV/atom (70 displacements per atom). On the other hand, SiC readily amorphized after damage levels of {similar_to}0.4 dpa at room temperature (RT). Si3N4 exhibited intermediate behavior; irradiation with Fe{sup 2+} ions at RT produced amorphization in the implanted ion region after damage levels of {similar_to}1 dpa. However, irradiated regions outside the implanted ion region did not amorphize even after damage levels > 5 dpa. The amorphous layer in the Fe-implanted region of Si3N4 did not appear if the specimen was simultaneoulsy irradiated with 1-MeV He{sup +} ions at RT. By comparison with published results, it is concluded that the implantation of certain chemical species has a pronounced effect on the amorphization threshold dose of all five materials. Intense ionizing radiation inhibits amorphization in Si3N4, but does not appear to significantly influence the amorphization of SiC.
- Research Organization:
- Oak Ridge National Lab., TN (United States)
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- AC05-96OR22464
- OSTI ID:
- 217727
- Report Number(s):
- CONF-950922--1; ON: DE96008694
- Country of Publication:
- United States
- Language:
- English
Similar Records
Threshold irradiation dose for amorphization of silicon carbide
Threshold irradiation dose for amorphization of silicon carbide