Comparison of the optical parameters of a CaF{sub 2} single crystal and optical ceramics
Journal Article
·
· Quantum Electronics (Woodbury, N.Y.)
- Institute of Applied Physics, Russian Academy of Sciences, Nizhnii Novgorod (Russian Federation)
- Research Institute of Optical Materials Technology, All-Russian Scientific Centre 'S.I. Vavilov State Optical Institute', St Petersburg (Russian Federation)
- Laser Materials and Technology Research Center, A. M. Prokhorov General Physics Institute, Russian Academy of Sciences, Moscow (Russian Federation)
Single crystal and optical ceramic CaF{sub 2} samples are studied by the method of thermally induced depolarisation of laser radiation at 1076 nm. The absorption coefficients of the single crystal and ceramics are estimated as {alpha} < 4.5x10{sup -4} cm{sup -1} and {alpha} < 1.33x10{sup -3} cm{sup -1}, respectively. (letters)
- OSTI ID:
- 21466593
- Journal Information:
- Quantum Electronics (Woodbury, N.Y.), Vol. 37, Issue 1; Other Information: DOI: 10.1070/QE2007v037n01ABEH013511; ISSN 1063-7818
- Country of Publication:
- United States
- Language:
- English
Similar Records
Optical absorption in CaF{sub 2} nanoceramics
A study of resistance of absorbing centres in a Pr{sup 2+}:CaF{sub 2} crystal to high-power laser radiation
The formation of metallic nanoparticles in single crystal CaF{sub 2} under 157 nm excimer laser irradiation
Journal Article
·
Sat Oct 31 00:00:00 EDT 2009
· Quantum Electronics (Woodbury, N.Y.)
·
OSTI ID:21466593
+9 more
A study of resistance of absorbing centres in a Pr{sup 2+}:CaF{sub 2} crystal to high-power laser radiation
Journal Article
·
Tue Jul 31 00:00:00 EDT 2001
· Quantum Electronics (Woodbury, N.Y.)
·
OSTI ID:21466593
The formation of metallic nanoparticles in single crystal CaF{sub 2} under 157 nm excimer laser irradiation
Journal Article
·
Wed Mar 01 00:00:00 EST 2006
· Journal of Applied Physics
·
OSTI ID:21466593
Related Subjects
75 CONDENSED MATTER PHYSICS
SUPERCONDUCTIVITY AND SUPERFLUIDITY
ABSORPTION
CALCIUM FLUORIDES
CERAMICS
COMPARATIVE EVALUATIONS
LASER RADIATION
MONOCRYSTALS
OPTICAL PROPERTIES
ALKALINE EARTH METAL COMPOUNDS
CALCIUM COMPOUNDS
CALCIUM HALIDES
CRYSTALS
ELECTROMAGNETIC RADIATION
EVALUATION
FLUORIDES
FLUORINE COMPOUNDS
HALIDES
HALOGEN COMPOUNDS
PHYSICAL PROPERTIES
RADIATIONS
SORPTION
SUPERCONDUCTIVITY AND SUPERFLUIDITY
ABSORPTION
CALCIUM FLUORIDES
CERAMICS
COMPARATIVE EVALUATIONS
LASER RADIATION
MONOCRYSTALS
OPTICAL PROPERTIES
ALKALINE EARTH METAL COMPOUNDS
CALCIUM COMPOUNDS
CALCIUM HALIDES
CRYSTALS
ELECTROMAGNETIC RADIATION
EVALUATION
FLUORIDES
FLUORINE COMPOUNDS
HALIDES
HALOGEN COMPOUNDS
PHYSICAL PROPERTIES
RADIATIONS
SORPTION