Structural and physical properties evolution of BaIr{sub 1-x}Mn{sub x}O{sub 3} solid solutions synthesized by high-pressure sintering
- Beijing National Lab for Condensed Matter Physics, Institute of Physics, Chinese Academy of Sciences, Beijing 100190 (China)
The BaIr{sub 1-x}Mn{sub x}O{sub 3} (0.0<=x<=1.0) solid solutions were synthesized by using the solid-state chemical method and high pressure sintering in the pressure range 0-5 GPa. According to the pressure-composition 'phase diagram' at 1000 deg. C, the 9M BaIr{sub 1-x}Mn{sub x}O{sub 3} transforms to the 6M form at 5 GPa and x<=1/6. In the x range 0.5-1.0, it transforms to the 9R form in a large pressure range. For the 9M BaIrO{sub 3}, the Mn ions substitution for Ir ions enhances the semiconducting property, and reduces the weak ferromagnetism. When x is larger than 1/3, the 9M/9R BaIr{sub 1-x}Mn{sub x}O{sub 3} behave spin-glass-like state at low temperature, with the glass transition temperature T{sub g} about 60 K. For the 6M BaIrO{sub 3}, the Mn ions doping results in that it transforms to insulator and spin-glass-like magnetism from the initial paramagnetic metal. - Graphical abstract: The BaRu{sub 1-x}Mn{sub x}O{sub 3} solid solutions were synthesized by using the solid-state chemical method and high-pressure sintering, and the pressure-composition 'phase diagram' at 1000 deg. C was obtained.
- OSTI ID:
- 21372545
- Journal Information:
- Journal of Solid State Chemistry, Vol. 183, Issue 3; Other Information: DOI: 10.1016/j.jssc.2010.01.019; PII: S0022-4596(10)00033-2; Copyright (c) 2010 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
Structural and magnetic properties of La{sub 1-x}Pr{sub x}MnO{sub 3+{delta}} (0{<=}x{<=}1.0)
High-pressure synthesis and characterization of BiCu{sub 3}(Mn{sub 4−x}Fe{sub x})O{sub 12} (x=0, 1.0, 2.0) complex perovskites
Related Subjects
ORGANIC
PHYSICAL AND ANALYTICAL CHEMISTRY
BARIUM COMPOUNDS
ELECTRIC CONDUCTIVITY
FERROMAGNETISM
GLASS
IRIDIUM COMPOUNDS
IRIDIUM IONS
MAGNETIC PROPERTIES
MANGANESE COMPOUNDS
MANGANESE IONS
OXIDES
PARAMAGNETISM
PEROVSKITE
PHASE DIAGRAMS
PRESSURE RANGE GIGA PA
SINTERING
SOLID SOLUTIONS
SPIN GLASS STATE
SYNTHESIS
TEMPERATURE RANGE 0013-0065 K
TEMPERATURE RANGE 1000-4000 K
ALKALINE EARTH METAL COMPOUNDS
CHALCOGENIDES
CHARGED PARTICLES
DIAGRAMS
DISPERSIONS
ELECTRICAL PROPERTIES
FABRICATION
HOMOGENEOUS MIXTURES
INFORMATION
IONS
MAGNETISM
MINERALS
MIXTURES
OXIDE MINERALS
OXYGEN COMPOUNDS
PEROVSKITES
PHYSICAL PROPERTIES
PRESSURE RANGE
REFRACTORY METAL COMPOUNDS
SOLUTIONS
TEMPERATURE RANGE
TRANSITION ELEMENT COMPOUNDS