Optical and electro-optic properties of micrometric thick lead zirconate titanate films on (Pb{sub 0.86},La{sub 0.14})TiO{sub 3}/glass
- School of Materials Science and Engineering, Nanyang Technological University, Singapore 639798 (Singapore)
Highly (100)-oriented Pb(Zr{sub 0.52},Ti{sub 0.48})O{sub 3} (PZT) films of up to approx2.4 mum are deposited on the (Pb{sub 0.86},La{sub 0.14})TiO{sub 3} (PLT)-coated amorphous substrate by one cycle of sputtering and annealing. The films possess fibrous columnar nanostructures and vertically grow on the PLT/glass substrate. Microstructure analysis and property characterization indicate that the films possess very promising optical, waveguiding, and electro-optic (EO) properties, as well as low propagation loss. The transparency of >80% in the range of lambda=400-1200 nm and the linear EO coefficient of 341.4 pm/V have been measured in the films. Due to the large EO coefficient and the micrometric thickness, a giant phase retardation of 2.93 rad has been measured under an electric field of 50 kV/mm.
- OSTI ID:
- 21359307
- Journal Information:
- Journal of Applied Physics, Vol. 106, Issue 2; Other Information: DOI: 10.1063/1.3176897; (c) 2009 American Institute of Physics; ISSN 0021-8979
- Country of Publication:
- United States
- Language:
- English
Similar Records
Ferroelectric and piezoelectric responses of (110) and (001)-oriented epitaxial Pb(Zr{sub 0.52}Ti{sub 0.48})O{sub 3} thin films on all-oxide layers buffered silicon
Low temperature synthesis of stoichiometric and homogeneous lead zirconate titanate powder by oxalate and hydroxide coprecipitation
Related Subjects
ANNEALING
CRYSTAL STRUCTURE
DEPOSITION
DIELECTRIC MATERIALS
ELECTRIC FIELDS
GLASS
MICROSTRUCTURE
NANOSTRUCTURES
OPACITY
PZT
RADIATION DOSE UNITS
SPUTTERING
SUBSTRATES
THIN FILMS
FILMS
HEAT TREATMENTS
LEAD COMPOUNDS
MATERIALS
OPTICAL PROPERTIES
OXYGEN COMPOUNDS
PHYSICAL PROPERTIES
TITANATES
TITANIUM COMPOUNDS
TRANSITION ELEMENT COMPOUNDS
UNITS
ZIRCONATES
ZIRCONIUM COMPOUNDS