Thermally induced evolution of morphology on ceramic surfaces in a thermionic converter
- Sandia National Laboratories P.O. Box 5800 Albuquerque, New Mexico 87185-0342 (United States)
The morphology of alumina and scandia ceramics exposed to controlled vacuum and diffusion modes in a thermionic converter has been studied. Evidence for vaporization at a temperature of 1770 K is manifest in the resulting surface morphologies of both ceramics, consistent with reported sample mass loss. Alumina shows intergranular relief with the formation of terrace-step structure on the grain surfaces. Terrace formation is not directly observed on scandia, however the development of vertical structure and maintenance of voids indicates that vaporization is initiated by structure at the grain edges. Extensive Sc{sub 2}O{sub 3} re-deposition occurs on the scandia surface, possibly mediated by the presence of molybdenum and tungsten. Evidence exists for refractory metal secondary phase formation in this deposit in the form of Sc{sub 6}MO{sub 12} (M=W or Mo). Alumina also shows evidence for materials' interactions in the form of tantalum assisted vaporization which significantly alters the terrace structure.
- OSTI ID:
- 21165735
- Journal Information:
- AIP Conference Proceedings, Journal Name: AIP Conference Proceedings Journal Issue: 1 Vol. 387; ISSN 0094-243X; ISSN APCPCS
- Country of Publication:
- United States
- Language:
- English
Similar Records
Thermally induced evolution of morphology on ceramic surfaces in a thermionic converter
CERAMIC TO METAL SEALS FOR HIGH-TEMPERATURE THERMIONIC CONVERTERS