Application of SP test to Evaluate Embrittlement of Dual Phase Stainless Steel Caused by Sigma Phase and Neutron Irradiation
- Department of Nuclear and Quantum Engineering, Korea Advanced Institute of Science and Technology, 373-1, Guseong- Dong, Yuseong-Gu, Daejeon, 305-701 (Korea, Republic of)
- Institute of Advanced Energy, Kyoto University, Gokasho, Uji, Kyoto 611-0011 (Japan)
The degradation of mechanical properties in dual phase 309L stainless steel RPV clad caused by the presence of s-phase as well as neutron irradiation was investigated using a small punch (SP) test. Two kinds of overlay-weld clad were fabricated on SA508 cl.3 pressure vessel steel plates with ER309L welding consumable strip by differing in heat input rates. The microstructure of the clad was composed of a main part of fcc austenite, a few percent of bcc d- ferrite and brittle bct s-phase. Area fraction of s-phase was ranging approximately 2 {approx} 8 percent depending on welding conditions. The JMTR was utilized for neutron irradiation and SP specimens were irradiated up to 1.02 x 10{sup 19} n/cm{sup 2} (E>1 MeV) at 563 K. After irradiation the SP ductile-to-brittle transition behavior moved to higher temperatures, however, it was more strongly affected by the amount of brittle s-phase rather than the irradiation at current doses. The cracking appearances in the SP specimens gradually changed from circumferential to radial cracking as the test temperature became low, content of {sigma}-phase increased and the specimens were irradiated. Those results were accounted for in terms of the inconsistency of fracture stress between the phases as well as the effects of stress-strain portioning combined with the changes of governing stress components for crack initiation. (authors)
- Research Organization:
- American Nuclear Society, 555 North Kensington Avenue, La Grange Park, IL 60526 (United States)
- OSTI ID:
- 21160684
- Resource Relation:
- Conference: ICAPP'04: 2004 international congress on advances in nuclear power plants, Pittsburgh, PA (United States), 13-17 Jun 2004; Other Information: Country of input: France; 10 refs; Related Information: In: Proceedings of the 2004 international congress on advances in nuclear power plants - ICAPP'04, 2338 pages.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Experimental and Computational Studies of Stress Corrosion Cracking of Alloys 308/309 and 82/182 Weldments in Corrosive and Radiation Environment
Small punch test evaluation of intergranular embrittlement of an alloy steel