Immobilization of radioactive and hazardous wastes in a developed sulfur polymer cement (SPC) matrix
- Atomic Energy Authority, Nasr City, P.O. Box 7551, Cairo (Egypt)
- National Research Center, Cairo (Egypt)
Available in abstract form only. Full text of publication follows: A process has been developed for the immobilization Cs, Sr, Ce, Pb, and Cr in forms that is non-dispersible and could be safely immobilized. The simulated radioactive wastes of Cs, Sr, and Ce, and the hazardous wastes of Cr, and Pb were immobilized in the stable form of sulfur polymer cement (SPC). In this process, the contaminants (in a single form) were added to the sulfur mixture of sulfur and aromatic /or aliphatic hydrocarbons that used as polymerizing agents for sulfur (95% S, and 5% organic polymer by weight). Durability of the fabricated SPC matrices was assessed in terms of their water of immersion, porosity, and compressive strength. The water immersion, and open porosity were found to be less than 2.5% for all the prepared matrices, whereas the compressive strength was in the range between 62.4 and 142.3 Kg.cm{sup -2}, depending on the composition of the prepared matrix. The prepared SPC matrices that characterized by X-ray diffraction (XRD) showed that the different added contaminants were stabilized during the solidification process during their reaction with sulfur and the organic polymer to form the corresponding metal sulfides. Toxicity Characteristic Leaching Procedure (TCLP), and the IAEA standard method have assessed the leachability of the prepared waste matrices. The TCLP results showed that most the concentration of the contaminants released were under their detection limit. The leach index for the investigated metals from the prepared SPC matrices was in the range of 9-11. The order of release of the investigated metals was Sr>Cs>Pb>Cr>Ce for the aliphatic polymer, and Sr>Cr>Pb>Cs>Ce for the aromatic one. The results obtained revealed a high performance for the prepared SPC matrices, as they are of low cost effect, highly available materials, and possessed good mechanical and leaching properties. Key Words: SPC/ Matrices/ Immobilization/ Wastes/ Leachability. (authors)
- Research Organization:
- American Society of Mechanical Engineers (ASME), Three Park Avenue, New York, NY 10016-5990 (United States); Technological Institute of the Royal Flemish Society of Engineers (TI-K VIV), Het Ingenieurshuis, Desguinlei 214, 2018 Antwerp (Belgium); Belgian Nuclear Society (BNS) - ASBL-VZW, c/o SCK-CEN, Avenue Hermann Debrouxlaan, 40 - B-1160 Brussels (Belgium)
- OSTI ID:
- 21156521
- Resource Relation:
- Conference: ICEM'07: 11. International Conference on Environmental Remediation and Radioactive Waste Management, Bruges (Belgium), 2-6 Sep 2007; Other Information: Country of input: France; Proceedings may be ordered from ASME Order Department, 22 Law Drive, P.O. Box 2300, Fairfield, NJ 07007-2300 (United States)
- Country of Publication:
- United States
- Language:
- English
Similar Records
Retention of Cr in Meta-kaolin-based geo-polymeric Materials under Oxidation and Carbonation - 17453
Cast Stone Oxidation Front Evaluation: Preliminary Results For Samples Exposed To Moist Air