Influence of stacking faults and alloy composition on irradiation induced amorphization of ZrCr{sub 2}, ZrFe{sub 2} and Zr{sub 3}(Fe{sub 1-x},Ni{sub x})
Conference
·
OSTI ID:211481
- Pennsylvania State Univ., University Park, PA (United States). Dept. of Nuclear Engineering
- Atomic Energy of Canada Ltd., Chalk River, ON (Canada). AECL Research
- Argonne National Lab., IL (United States). Materials Science Div.
These Zr-based intermetallics were irradiated with high-energy electrons at the ANL HVEM/Tandem facility. Although ZrCr{sub 2} and ZrFe{sub 2} have the same Laves phase C15 fcc crystal structure, their critical temperatures for amorphization under electron irradiation were 180 and 80 K, showing that Cr substitution for Fe in the sublattice had a marked effect on annealing. The low temperature dose to amorphization was higher in ZrFe{sub 2} than in ZrCr{sub 2} by a factor of two. Presence of a high density of stacking faults had a strong effect on amorphization in both compounds causing the critical temperature to be increased by 10-15 K. By contrast, addition of Ni to Zr{sub 3}(Fe{sub 1-x},Ni{sub x}) had no effect on amorphization behavior for x=0.1 and 0.5. These results are discussed in terms of current models of amorphization based on defect accumulation and attainment of a critical damage level, such as given by the Lindemann criterion.
- Research Organization:
- Argonne National Lab., IL (United States). Materials Science Div.
- Sponsoring Organization:
- USDOE, Washington, DC (United States); Atomic Energy of Canada Ltd., Montreal, PQ (Canada). CANDU Operations
- DOE Contract Number:
- W-31109-ENG-38
- OSTI ID:
- 211481
- Report Number(s):
- ANL/MSD/CP--88674; CONF-951155--72; ON: DE96006743
- Country of Publication:
- United States
- Language:
- English
Similar Records
CONSTITUTION DIAGRAM OF ZrCr$sub 2$-ZrFe$sub 2$ ALLOYS
Slip, twinning and transformation in Laves phases. [Ti-TiCr[sub 2]; Fe-ZrFe[sub 2]; Ni-Cu-Mg containing MgNi[sub 2] and MgCu[sub 2]]
Amorphization kinetics of Zr(Cr,Fe)[sub 2] under ion irradiation
Journal Article
·
Sun Dec 31 23:00:00 EST 1961
· Sbornik Nauchnykh Trudov Instituta Metallofiziki, Akademiya Nauk Ukrainskoi SSR (Ukrainian S.S.R.)S.R.)
·
OSTI ID:4747189
Slip, twinning and transformation in Laves phases. [Ti-TiCr[sub 2]; Fe-ZrFe[sub 2]; Ni-Cu-Mg containing MgNi[sub 2] and MgCu[sub 2]]
Technical Report
·
Mon Jan 25 23:00:00 EST 1993
·
OSTI ID:6310651
Amorphization kinetics of Zr(Cr,Fe)[sub 2] under ion irradiation
Conference
·
Mon Nov 30 23:00:00 EST 1992
·
OSTI ID:6774091