Selected-control synthesis of dysprosium hydroxide and oxide nanorods by adjusting hydrothermal temperature
Journal Article
·
· Materials Research Bulletin
- Coll Chem Engn and Mat Sci, Zhejiang Univ Technol, Hangzhou, Zhejiang 310014 (China)
- Department of Chemistry, Fujian Normal University, Fuzhou 350007 (China)
Dysprosium hydroxide and oxide nanorods were prepared directly from commercial bulk Dy{sub 2}O{sub 3} crystals by facile hydrothermal process at 130 and 210 deg. C, respectively. The as-synthesized dysprosium hydroxide and oxide nanorods were investigated by various techniques of XRD, TEM, SEM, and EDS. In the process, the temperature was found to play important roles in determining produce dysprosium hydroxide and oxide nanorods.
- OSTI ID:
- 21143987
- Journal Information:
- Materials Research Bulletin, Vol. 43, Issue 5; Other Information: DOI: 10.1016/j.materresbull.2007.06.007; PII: S0025-5408(07)00243-7; Copyright (c) 2007 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
CTAB assisted hydrothermal synthesis, controlled conversion and CO oxidation properties of CeO{sub 2} nanoplates, nanotubes, and nanorods
Microwave-assisted hydrothermal synthesis of coralloid nanostructured nickel hydroxide hydrate and thermal conversion to nickel oxide
Characterization and adsorption performance of Pb(II) on CuO nanorods synthesized by the hydrothermal method
Journal Article
·
Sun Jun 15 00:00:00 EDT 2008
· Journal of Solid State Chemistry
·
OSTI ID:21143987
Microwave-assisted hydrothermal synthesis of coralloid nanostructured nickel hydroxide hydrate and thermal conversion to nickel oxide
Journal Article
·
Thu Oct 15 00:00:00 EDT 2009
· Materials Research Bulletin
·
OSTI ID:21143987
+2 more
Characterization and adsorption performance of Pb(II) on CuO nanorods synthesized by the hydrothermal method
Journal Article
·
Thu Oct 15 00:00:00 EDT 2015
· Materials Research Bulletin
·
OSTI ID:21143987
+2 more