Effects of heat input on microstructure and tensile properties of laser welded magnesium alloy AZ31
- School of Materials Science and Engineering, Hunan University, Changsha 410082 (China)
A 3 kW CO{sub 2} laser beam was used to join wrought magnesium alloy AZ31 sheets, and the effects of heat input on the quality of butt welding joints were studied. By macro and microanalysis, it is found that the welding heat input plays an important role in laser welding process for AZ31 wrought sheets. After welding, the grains far from the weld centre present the typical rolled structure. But the microstructure out of the fusion zone gradually changes to complete equiaxed crystals as the distance from the weld centre decreases. Adjacent to the fusion boundary, there is a band region with columnar grains, and its growth direction is obviously perpendicular to the solid/liquid line. The microstructure in fusion centre consists of fine equiaxed grains and the many precipitated particles are brittle phase Mg{sub 17}Al{sub 12} or Mg{sub 17}(Al,Zn){sub 12}. With increasing the heat input, the band width of columnar grains varies, the grains in fusion zone get coarser, and the distribution of precipitates changes from intragranularly scattered particles to intergranularly packed ones. The results of tensile test show that the change trend of ultimate tensile strength (UTS) and elongation of the welded joints is to increase at first and then decrease with the heat input increasing. When the heat input reaches 24 J mm{sup -1}, the maximum value of the UTS is up to 96.8% of the base metal.
- OSTI ID:
- 21137469
- Journal Information:
- Materials Characterization, Journal Name: Materials Characterization Journal Issue: 10 Vol. 59; ISSN 1044-5803; ISSN MACHEX
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effect of heat input on the microstructure and mechanical properties of tungsten inert gas arc butt-welded AZ61 magnesium alloy plates
Microstructure and Mechanical Properties of Al-Mg-Sc-Zr Alloy Variable Polarity Plasma Arc Welding Joint