Reduction of iron-oxide-carbon composites: part III. Shrinkage of composite pellets during reduction
- Praxair Inc., Tonawanda, NY (United States). Praxair Technological Center
This article involves the evaluation of the volume change of iron-oxide-carbon composite pellets and its implications on reduction kinetics under conditions prevalent in a rotary hearth furnace (RHF) that were simulated in the laboratory. The pellets, in general, were found to shrink considerably during the reduction due to the loss of carbon and oxygen from the system, sintering of the iron-oxide, and formation of a molten slag phase at localized regions inside the pellets due to the presence of binder and coal/wood-charcoal ash at the reduction temperatures. One of the shortcomings of the RHF ironmaking process has been the inability to use multiple layers of composite pellets because of the impediment in heat transport to the lower layers of a multilayer bed. However, pellet shrinkage was found to have a strong effect on the reduction kinetics by virtue of enhancing the external heat transport to the lower layers. The volume change of the different kinds of composite pellets was studied as a function of reduction temperature and time. The estimation of the change in the amount of external heat transport with varying pellet sizes for a particular layer of a multilayer bed was obtained by conducting heat-transfer tests using inert low-carbon steel spheres. It was found that if the pellets of the top layer of the bed shrink by 30 pct, the external heat transfer to the second layer increases by nearly 6 times.
- OSTI ID:
- 21126141
- Journal Information:
- Metallurgical and Materials Transactions B: Process Metallurgy and Materials Processing Science, Vol. 39, Issue 6; ISSN 1073-5615
- Country of Publication:
- United States
- Language:
- English
Similar Records
Reduction of iron-oxide-carbon composites: part I. Estimation of the rate constants
Rate of reduction of ore-carbon composites: Part II. Modeling of reduction in extended composites