Joining of Ni-TiC FGM and Ni-Al Intermetallics by Centrifugal Combustion Synthesis
- Hokkaido University, Kita 13, Nishi 8, Kita-ku, Sapporo, Hokkaido, 060-8628 (Japan)
- Graduate Student of Hokkaido University (Japan)
A centrifugal combustion synthesis (CCS) process has been investigated to join a Ni-Al intermetallic compound and a Ni-TiC cermet. The cermet, a tubular graphite mold, and a green compact of reactants consisting of Al, Ni and NiO were set in a centrifugal caster. When the combustion synthesis reaction was induced in the centrifugal force field, a synthesized molten Ni-Al alloy flowed into the graphite mold and joined to the cermet. The soundness of the joint interface depended on the volume percentage of TiC phase in the cermet. A lot of defects were formed near the interface between the Ni-TiC cermet and the cast Ni-Al alloy when the volume percentage of TiC was 50% or higher. For this kind of cermet system, using a functionally graded cermet such as Ni-10 vol.%TiC/Ni-25 vol.%TiC/Ni-50 vol.%TiC overcame this difficulty. The four-point bending strength of the joined specimen consisting of the three-layered FGM cermet and cast Ni-29 mol%Al alloy was 1010 MPa which is close to the result for a Ni-29 mol%Al alloy specimen.
- OSTI ID:
- 21055266
- Journal Information:
- AIP Conference Proceedings, Vol. 973, Issue 1; Conference: M and FGM 2006: Conference on multiscale and funtionally graded materials 2006, Oahu Island, HI (United States), 15-18 Oct 2006; Other Information: DOI: 10.1063/1.2896841; (c) 2008 American Institute of Physics; Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
PROGRESS RELATING TO CIVILIAN APPLICATIONS DURING JANUARY 1959
PROGRESS RELATING TO CIVILIAN APPLICATIONS DURING DECEMBER, 1958