Preparation and Fatigue Properties of Functionally Graded Cemented Carbides
- State Key Lab of Powder Metallurgy, Central South University, Changsha 410083 (China)
- Department of Materials Science and Engineering, University of Tennessee, Knoxville, TN 37996 (United States)
Cemented carbides with a functionally graded structure have significantly improved mechanical properties and lifetimes in cutting, drilling and molding. In this work, WC-6 wt.% Co cemented carbides with three-layer graded structure (surface layer rich in WC, mid layer rich in Co and the inner part of the average composition) were prepared by carburizing pre-sintered {eta}-phase-containing cemented carbides. The three-point bending fatigue tests based on the total-life approach were conducted on both WC-6wt%Co functionally graded cemented carbides (FGCC) and conventional WC-6wt%Co cemented carbides. The functionally graded cemented carbide shows a slightly higher fatigue limit ({approx}100 MPa) than the conventional ones under the present testing conditions. However, the fatigue crack nucleation behavior of FGCC is different from that of the conventional ones. The crack nucleates preferentially along the Co-gradient and perpendicular to the tension surface in FGCC, while parallel to the tension surface in conventional cemented carbides.
- OSTI ID:
- 21055264
- Journal Information:
- AIP Conference Proceedings, Vol. 973, Issue 1; Conference: M and FGM 2006: Conference on multiscale and funtionally graded materials 2006, Oahu Island, HI (United States), 15-18 Oct 2006; Other Information: DOI: 10.1063/1.2896839; (c) 2008 American Institute of Physics; Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Elastic-Plastic Constitutive Equation of WC-Co Cemented Carbides with Anisotropic Damage
Rolling contact fatigue characteristics of thermal sprayed tungsten carbide coatings