Wetting behavior of molten In-Sn alloy on bulk amorphous and crystalline Cu{sub 40}Zr{sub 44}Al{sub 8}Ag{sub 8}
- Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016 (China)
Using the sessile-drop method, the wettability of the molten In-Sn alloy on bulk amorphous and crystalline Cu{sub 40}Zr{sub 44}Al{sub 8}Ag{sub 8} alloy was studied at different temperatures. It was found that the equilibrium contact angle of In-Sn alloy melt on bulk amorphous substrate was smaller than that of the crystalline one. An intermetallic compound existed at the interface of In-Sn alloy on amorphous Cu{sub 40}Zr{sub 44}Al{sub 8}Ag{sub 8}, while no intermediate reaction layer was formed at the interface of In-Sn alloy on crystalline Cu{sub 40}Zr{sub 44}Al{sub 8}Ag{sub 8} in the temperature range studied.
- OSTI ID:
- 21013757
- Journal Information:
- Applied Physics Letters, Journal Name: Applied Physics Letters Journal Issue: 18 Vol. 91; ISSN APPLAB; ISSN 0003-6951
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effect of Sn addition on the glass-forming ability in (Cu{sub 40}Ti{sub 30}Ni{sub 15}Zr{sub 10}){sub (100{minus}x)/95}Sn{sub x} (x = 0, 2, 4, 6 and 8) alloys
Effect of cooling rate on the microstructure and microhardness of the CuZrAgAl alloy
Design of Cu{sub 8}Zr{sub 5}-based bulk metallic glasses
Journal Article
·
Wed May 10 00:00:00 EDT 2000
· Scripta Materialia
·
OSTI ID:20075981
Effect of cooling rate on the microstructure and microhardness of the CuZrAgAl alloy
Journal Article
·
Wed Aug 15 00:00:00 EDT 2012
· Materials Characterization
·
OSTI ID:22066476
Design of Cu{sub 8}Zr{sub 5}-based bulk metallic glasses
Journal Article
·
Mon Jun 12 00:00:00 EDT 2006
· Applied Physics Letters
·
OSTI ID:20779397