Reactive pozzolana from Indian clays-their use in cement mortars
- Environmental S and T Division, Central Building Research Institute, Roorkee-247667, Uttranchal State (India)
Studies were undertaken to produce reactive pozzolana i.e. metakaolin from four kaolinitic clays collected from different sources in India. The metakaolin produced from these clays at 700-800 deg. C show lime reactivity in between 10.5 to 11.5 N/mm{sup 2} which is equivalent to commercially available calcined clay Metacem-85. The microstructure of the metakaolin has been reported. The effect of addition of metakaolin up to 25% in the Portland cement mortars was investigated. An increase in compressive strength and decrease of porosity and pore diameter of cement mortars containing metakaolin (10%) was noted over the cement mortars without metakaolin. The hydration of metakaolin blended cement mortars was investigated by differential thermal analysis (DTA) and scanning electron microscopy (SEM). The major hydraulic products like C-S-H and C{sub 4}AH{sub 13} have been identified. Durability of the cement mortars with and without metakaolin was examined in different sulphate solutions. Data show better strength achievement in cement mortars containing 10% MK than the OPC mortars alone.
- OSTI ID:
- 20871541
- Journal Information:
- Cement and Concrete Research, Vol. 36, Issue 10; Other Information: DOI: 10.1016/j.cemconres.2004.12.002; PII: S0008-8846(04)00512-5; Copyright (c) 2006 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved; Country of input: International Atomic Energy Agency (IAEA); ISSN 0008-8846
- Country of Publication:
- United States
- Language:
- English
Similar Records
Formulating a low-alkalinity, high-resistance and low-heat concrete for radioactive waste repositories
The effect of high curing temperature on the reaction kinetics in MK/lime and MK-blended cement matrices at 60 deg. C