Optimizing High-Z Coatings for Inertial Fusion Energy Shells
- University of California (United States)
- General Atomics (United States)
Inertial fusion energy (IFE) reactors require shells with a high-Z coating that is both permeable, for timely filling with deuterium-tritium, and reflective, for survival in the chamber. Previously, gold was deposited on shells while they were agitated to obtain uniform, reproducible coatings. However, these coatings were rather impermeable, resulting in unacceptably long fill times. We report here on an initial study on Pd coatings on shells in the same manner. We have found that these palladium-coated shells are substantially more permeable than gold. Pd coatings on shells remained stable on exposure to deuterium. Pd coatings had lower reflectivity compared to gold that leads to a lower working temperature, and efficiency, of the proposed fusion reactor. Seeking to combine the permeability of Pd coatings and high reflectivity of gold, AuPd-alloy coatings were produced using a cosputtering technique. These alloys demonstrated higher permeability than Au and higher reflectivity than Pd. However, these coatings were still less reflective than the gold coatings. To improve the permeability of gold's coatings, permeation experiments were performed at higher temperatures. With the parameters of composition, thickness, and temperature, we have the ability to comply with a large target design window.
- OSTI ID:
- 20845901
- Journal Information:
- Fusion Science and Technology, Journal Name: Fusion Science and Technology Journal Issue: 3 Vol. 43; ISSN 1536-1055
- Country of Publication:
- United States
- Language:
- English
Similar Records
FABRICATION OF GAS-FILLED TUNGSTEN-COATED GLASS SHELLS
Volcano‐like Activity Trends in Au@Pd Catalysts: The Role of Pd Loading and Nanoparticle Size