Interdependence between stress, preferred orientation, and surface morphology of nanocrystalline TiN thin films deposited by dual ion beam sputtering
- Laboratoire de Metallurgie Physique, UMR CNRS 6630, Universite de Poitiers, SP2MI, Teleport 2, BP 30179, 86962 Futuroscope-Chasseneuil Cedex (France)
To clarify the underlying mechanisms that cause the preferred orientation in TiN films, we investigated the evolution with the thickness of the texture, surface morphology, and residual stress in TiN thin films deposited by dual ion beam sputtering. The films, with thickness h ranging from 50 to 300 nm, were grown on oxidized Si substrates using a primary Ar ion beam accelerated under 1.2 kV and different voltages V{sub a} of the (Ar+N{sub 2}) assistance beam: 25, 50, and 150 V. The influence of temperature was also investigated by varying the substrate temperature T{sub s} (25-300 deg. C) during growth or by performing a postdeposition annealing. X-ray diffraction (XRD) as well as transmission electron microscopy were used to study the microstructure and changes of texture with thickness h, while x-ray reflectivity and atomic force microscopy measurements were performed to determine the surface roughness. Residual stresses were measured by XRD and analyzed using a triaxial stress model. The crystallite group method was used for a strain determination of crystallites having different fiber axis directions, i.e., when a mixed texture exists. The surface roughness is found to increase with V{sub a} and T{sub s} due to the resputtering effect of the film surface. XRD reveals that for a small thickness (h{approx}50 nm) the TiN films exhibit a strong (002) texture independent of V{sub a}. For a larger thickness (100<h<300 nm), the development of a (111) preferred orientation is observed together with a grain size increase, except at T{sub s}=300 deg. C, where the predominant texture remains (002). A minor (220) texture is also found, but its contribution strongly decreases with V{sub a} and T{sub s}. The residual stresses are highly compressive, ranging from -8 to -5 GPa, depending on the deposition conditions. When a mixed texture exists, the analysis reveals that (111)-oriented grains sustain stresses that are about 20% more compressive than those sustained by (002)-oriented grains. The present results suggest that the change in the preferred orientation from (002) to (111) is not correlated with a strain energy minimization or with a systematic increase in surface morphology. Rather, kinetically driven mechanisms occurring during growth and linked to anisotropies in surface diffusivities, adatom mobilities, and collisional cascades effects are likely to control the texture development in TiN thin films produced with energetic ionic species. This interpretation is supported by in situ temperature XRD measurements.
- OSTI ID:
- 20795831
- Journal Information:
- Journal of Applied Physics, Vol. 99, Issue 11; Other Information: DOI: 10.1063/1.2197287; (c) 2006 American Institute of Physics; Country of input: International Atomic Energy Agency (IAEA); ISSN 0021-8979
- Country of Publication:
- United States
- Language:
- English
Similar Records
Development of preferred orientation in polycrystalline TiN layers grown by ultrahigh vacuum reactive magnetron sputtering
Growth of poly- and single-crystal ScN on MgO(001): Role of low-energy N{sub 2}{sup +} irradiation in determining texture, microstructure evolution, and mechanical properties
Related Subjects
ANISOTROPY
ANNEALING
ARGON IONS
ATOMIC FORCE MICROSCOPY
DEPOSITION
GRAIN ORIENTATION
GRAIN SIZE
ION BEAMS
MORPHOLOGY
NANOSTRUCTURES
PRESSURE RANGE GIGA PA
RESIDUAL STRESSES
SPUTTERING
TEMPERATURE DEPENDENCE
TEMPERATURE RANGE 0273-0400 K
TEMPERATURE RANGE 0400-1000 K
THIN FILMS
TITANIUM NITRIDES
TRANSMISSION ELECTRON MICROSCOPY
X-RAY DIFFRACTION