Metal phosphonates based on aminomethylenediphosphonate: Syntheses and characterization of Na{sub 4}Zn{l_brace}NH{sub 3}CH(PO{sub 3}){sub 2}{r_brace}{sub 2}.4H{sub 2}O, Ni{l_brace}NH{sub 3}CH(PO{sub 3}H){sub 2}{r_brace}{sub 2}.xH{sub 2}O and NaNi{sub 2}{l_brace}NH{sub 3}CH(PO{sub 3})(PO{sub 3}H{sub 0.5}){r_brace}{sub 2}(H{sub 2}O){sub 2}.2H{sub 2}O

Journal Article · Wed Feb 15 04:00:00 EST 2006 · Journal of Solid State Chemistry

OSTI ID:20784877

Songsong, Bao ^[1]; Tianwei, Wang ^[1]; Yizhi, Li ^[1]; Limin, Zheng ^[1]

---

1. State Key Laboratory of Coordination Chemistry, Coordination Chemistry Institute, Nanjing University, Nanjing 210093 (China)

This paper describes the syntheses of three transition metal diphosphonate compounds: Na{sub 4}Zn{l_brace}NH{sub 3}CH(PO{sub 3}){sub 2}{r_brace}{sub 2}.4H{sub 2}O (1), Ni{l_brace}NH{sub 3}CH(PO{sub 3}H){sub 2}{r_brace}{sub 2}.xH{sub 2}O (2) and NaNi{sub 2}{l_brace}NH{sub 3}CH(PO{sub 3})(PO{sub 3}H{sub 0.5}){r_brace}{sub 2}(H{sub 2}O){sub 2}.2H{sub 2}O (3). Compound 1 contains chains of [Zn{l_brace}NH{sub 3}CH(PO{sub 3}){sub 2}{r_brace}{sub 2}]{sub n}{sup 4n-} made up of corner-sharing ZnO{sub 6} octahedra and CPO{sub 3} tetrahedra, which are further connected by tetramers of edge-sharing NaO{sub 6} octahedra, forming a three-dimensional open-framework structure. Compound 2 shows a square-grid layer structure where the NiO{sub 6} octahedra are corner shared with CPO{sub 3} tetrahedra. The adjacent layers are linked by strong inter-layer hydrogen bonds, resulting in a three-dimensional open-network structure with channels where the lattice water molecules reside. The structure of compound 3 is analogous to that of NaCo{sub 2}{l_brace}NH{sub 3}CH(PO{sub 3})(PO{sub 3}H{sub 0.5}){r_brace}{sub 2}(H{sub 2}O){sub 2}.xH{sub 2}O in which layers of Ni{sub 2}{l_brace}NH{sub 3}CH(PO{sub 3})(PO{sub 3}H{sub 0.5}){r_brace}{sub 2}(H{sub 2}O){sub 2} are connected by NaO{sub 6} linkages into an open-framework structure. The magnetic studies show that weak antiferromagnetic interactions are mediated between the nickel ions in compounds 2 and 3. Crystal data for 1: triclinic, space group P-1, a=5.551(2)A, b=6.166(2)A, c=12.424(4)A, {alpha}=92.422(6){sup o}, {beta}=92.687(7){sup o}, {gamma}=93.926(6){sup o}, V=423.3(2)A{sup 3}, Z=2. For 2: triclinic, space group P-1, a=9.043(1)A, b=9.180(1)A, c=9.271(1)A, {alpha}=89.693(3){sup o}, {beta}=70.202(3){sup o}, {gamma}=89.530(3){sup o}, V=724.1(2)A{sup 3}, Z=2.

• OSTI ID: 20784877
• Journal Information: Journal of Solid State Chemistry, Journal Name: Journal of Solid State Chemistry Journal Issue: 2 Vol. 179; ISSN 0022-4596; ISSN JSSCBI
• Country of Publication: United States
• Language: English

Related Subjects

36 MATERIALS SCIENCE
ANTIFERROMAGNETISM
CRYSTAL STRUCTURE
LAYERS
NICKEL COMPOUNDS
NICKEL IONS
PHOSPHONATES
SODIUM COMPOUNDS
SPACE GROUPS
SYNTHESIS
ZINC COMPOUNDS