Microstructural evolution of Alloy 690 during sensitization at 700 deg. C
A structural characterization of sensitized Alloy 690 has been carried out. Alloy 690 was solution annealed (SA; 1100 deg. C for 30 min, water quenched, WQ) and sensitized at 700 deg. C for 5, 12, 24, 36, 48 and 72 h, followed by water quenched. Techniques employed included scanning electron microscope (SEM), transmission electron microscopy (TEM), X-ray diffraction and corrosion weight-loss tests. It was found that the cubic Cr{sub 0.19}Fe{sub 0.7}Ni{sub 0.11} phase was the main component in all the conditions. In addition, a grain refinement was observed when the aging time was increased; but after 48 h of aging, a discrete, semicontinuous network of Cr{sub 23}C{sub 6} precipitates was detected by X-ray diffraction, in addition to the NiCrO{sub 4}, Ni{sub 9}S{sub 8} and (Fe,Ni){sub 9}S{sub 8} phases found by TEM at the grain boundaries, making this alloy more susceptible to intergranular attack (IGA). After 72 h of aging, chromium continues diffusing, 'back-filling' the prior depletion profile, recovering the IGA resistance.
- OSTI ID:
- 20748728
- Journal Information:
- Materials Characterization, Vol. 51, Issue 5; Other Information: DOI: 10.1016/j.matchar.2004.01.004; PII: S1044580304000245; Copyright (c) 2004 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved; Country of input: International Atomic Energy Agency (IAEA); ISSN 1044-5803
- Country of Publication:
- United States
- Language:
- English
Similar Records
Clarification of stress corrosion cracking mechanism on nickel base alloys in steam generators for their long lifetime assurance
CHEMICAL ENGINEERING DIVISION SUMMARY REPORT FOR APRIL, MAY, JUNE 1960