Etching of high aspect ratio features in Si using SF{sub 6}/O{sub 2}/HBr and SF{sub 6}/O{sub 2}/Cl{sub 2} plasma

Journal Article · Tue Nov 15 04:00:00 EST 2005 · Journal of Vacuum Science and Technology. A, Vacuum, Surfaces and Films

DOI:https://doi.org/10.1116/1.2049303· OSTI ID:20723206

Gomez, Sergi; Belen, Rodolfo Jun; Kiehlbauch, Mark; Aydil, Eray S ^[1]

---

1. Department of Chemical Engineering, University of California, Santa Barbara, Santa Barbara, California 93106 (United States)

We have investigated the etching of high aspect ratio holes ({approx}4 {mu}m deep, {approx}0.2 {mu}m diameter) in silicon using plasmas maintained in mixtures of SF{sub 6}, O{sub 2}, and HBr or Cl{sub 2} gases. The etching experiments were conducted in a low pressure (25 mTorr), high density, inductively coupled plasma etching reactor with a planar coil. Visualization of the profiles with scanning electron microscopy is used in conjunction with plasma diagnostics such as optical emission and mass spectroscopies to understand the key factors that control the feature profile shape and etch rate. HBr addition to SF{sub 6}/O{sub 2} mixture reduces the F-to-O ratio, increases sidewall passivation and reduces mask undercut. Addition of Cl{sub 2} to SF{sub 6}/O{sub 2} discharge also decreases the F-to-O ratio, but Cl-enhanced F chemical etching of silicon significantly increases the mask undercut and lateral etching. In both SF{sub 6}/O{sub 2}/HBr and SF{sub 6}/O{sub 2}/Cl{sub 2} mixtures, reduction of O{sub 2} flow rate and subsequent increase of the halogen-to-O ratio eventually results in significant lateral etching because of the lack of oxygen required to form a siliconoxyhalide passivating film on the sidewalls.

• OSTI ID: 20723206
• Journal Information: Journal of Vacuum Science and Technology. A, Vacuum, Surfaces and Films, Journal Name: Journal of Vacuum Science and Technology. A, Vacuum, Surfaces and Films Journal Issue: 6 Vol. 23; ISSN 0734-2101; ISSN JVTAD6
• Country of Publication: United States
• Language: English

Related Subjects

70 PLASMA PHYSICS AND FUSION TECHNOLOGY
ASPECT RATIO
CHLORINE
ETCHING
FLOW RATE
GASES
HYDROBROMIC ACID
MASS SPECTROSCOPY
OXYGEN
PASSIVATION
PLASMA
PLASMA DENSITY
PLASMA DIAGNOSTICS
PLASMA PRESSURE
PRESSURE RANGE PA
SCANNING ELECTRON MICROSCOPY
SEMICONDUCTOR MATERIALS
SILICON
SULFUR FLUORIDES