Characterisation of Corrosion Products on Iron in Contact With Hot Water
- Department of Physics, University of Parma, Parma (Italy)
- Italy
- Institute of Metallurgy, University of Bologna, Bologna (Italy)
The corrosion of galvanised sheets of carbon steel in contact with hot water in two household systems was investigated by means of metallographic techniques, X-ray diffraction analysis and trasmission Moessbauer spectroscopy. The corrosion process gave rise to localised attack of the inner wall of the steel sheets, with formation of tubercules of reaction products in zones where the protective effect of the zinc coating vanished, probably for an excessive increase in the heating temperature leading zinc to become cathodic to iron. Significant differences were found in the phase composition of the corrosion products depending on the in-service life of the steel component. After {approx}1 year of exposure to hot water, siderite and lepidocrocite were found to be the prevailing corrosion products, formed together with lower amounts of akaganeite, mixed Zn-Fe carbonate and hydrozincite. After about a double exposure time to hot water, the corrosion products were mainly constituted by magnetite, siderite and lepidocrocite, together with lower amounts of goethite, akaganeite, Zn-Fe carbonate and hydrozincite. A complementary use of X-ray diffraction and Moessbauer techniques proved to be determining for a satisfactory identification of the corrosion products.
- OSTI ID:
- 20722169
- Journal Information:
- AIP Conference Proceedings, Journal Name: AIP Conference Proceedings Journal Issue: 1 Vol. 765; ISSN APCPCS; ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Corrosion of Submerged Artifacts and the Conservation of the USS Monitor
Zinc immobilization and magnetite formation via ferric oxide reduction by Shewanella putrefaciens 200