Development of high permeability nanocrystalline permalloy by electrodeposition
Journal Article
·
· Journal of Applied Physics
- Department of Mechanical Engineering, National University of Singapore, Singapore 119260 (Singapore)
In this study, for developing microsensors for weak magnetic field, methods for developing high permeability nanocrystalline permalloy by electrodeposition and the relationship between the grain size and magnetic properties of the nanocrystalline permalloy are investigated. By dc plating with and without saccharin added and pulse plating with saccharin added, permalloy samples of grain sizes from 52 nm to 11 nm are obtained. The coercivity and magnetoimpedance (MI) ratio of the samples are tested against the grain size variation. Results show that the coercivity decreases rapidly and MI ratio increases greatly with grain size decrease from 52 nm to 11 nm.
- OSTI ID:
- 20711682
- Journal Information:
- Journal of Applied Physics, Journal Name: Journal of Applied Physics Journal Issue: 10 Vol. 97; ISSN JAPIAU; ISSN 0021-8979
- Country of Publication:
- United States
- Language:
- English
Similar Records
Electroplating of low stress permalloy for MEMS
The influence of Mo addition on the microstructure and its thermal stability for electrodeposited Ni films
Effect of electrodeposition temperature on grain orientation and corrosion resistance of nanocrystalline pure nickel
Journal Article
·
Tue Aug 15 00:00:00 EDT 2006
· Materials Characterization
·
OSTI ID:20889844
The influence of Mo addition on the microstructure and its thermal stability for electrodeposited Ni films
Journal Article
·
Wed Nov 14 23:00:00 EST 2018
· Materials Characterization
·
OSTI ID:22805891
Effect of electrodeposition temperature on grain orientation and corrosion resistance of nanocrystalline pure nickel
Journal Article
·
Mon Aug 15 00:00:00 EDT 2016
· Journal of Solid State Chemistry
·
OSTI ID:22584185