Autogenous shrinkage in high-performance cement paste: An evaluation of basic mechanisms
In this paper, various mechanisms suggested to cause autogenous shrinkage are presented. The mechanisms are evaluated from the point of view of their soundness and applicability to quantitative modeling of autogenous shrinkage. The capillary tension approach is advantageous, because it has a sound mechanical and thermodynamical basis. Furthermore, this mechanism is easily applicable in a numerical model when dealing with a continuously changing microstructure. In order to test the numerical model, autogenous deformation and internal relative humidity (RH) of a Portland cement paste were measured during the first week of hardening. The isothermal heat evolution was also recorded to monitor the progress of hydration and the elastic modulus in compression was measured. RH change, degree of hydration and elastic modulus were used as input data for the calculation of autogenous deformation based on the capillary tension approach. Because a part of the RH drop in the cement paste is due to dissolved salts in the pore solution, a method is suggested to separate this effect from self-desiccation and to calculate the actual stress in the pore fluid associated with menisci formation.
- OSTI ID:
- 20658292
- Journal Information:
- Cement and Concrete Research, Vol. 33, Issue 2; Other Information: PII: S0008884602008906; Copyright (c) 2002 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved; Country of input: International Atomic Energy Agency (IAEA); ISSN 0008-8846
- Country of Publication:
- United States
- Language:
- English
Similar Records
Analyses and models of the autogenous shrinkage of hardening cement paste. 2: Modelling at scale of hydrating grains
Temperature dependence of autogenous shrinkage of silica fume cement pastes with a very low water–binder ratio