Characterization of Retrogression and Re-Aging Heat Treatment of AA7075-T6 Using Nonlinear Acoustics and Eddy Current
Journal Article
·
· AIP Conference Proceedings
- Center for Materials Diagnostics, University of Dayton Research Institute, Dayton, Ohio 45469 (United States)
- Structural Integrity Division, University of Dayton Research Institute, Dayton, Ohio 45469 (United States)
- Metals, Ceramics, and NDE Division, Air Force Research Laboratory, Wright-Patterson Air Force Base, OH 45433 (United States)
Nonlinear acoustic parameter and eddy current methods have been utilized to characterize the heat treatment process of retrogression and re-aging of aluminum 7075-T6. The results of nonlinear acoustic parameter measurements show two distinct peaks at 30 minutes and 45 minutes of retrogression time. The phase of the through-thickness eddy current signal shows a minimum at 42 minutes of retrogression time. Application of combined methods for identifying the optimized properties in the material is discussed.
- OSTI ID:
- 20632898
- Journal Information:
- AIP Conference Proceedings, Vol. 700, Issue 1; Conference: 30. annual review of progress in quantitative nondestructive evaluation, Green Bay, WI (United States), 27 Jul - 1 Aug 2003; Other Information: DOI: 10.1063/1.1711742; (c) 2004 American Institute of Physics; Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Assessment of retrogression and re-aging treatment on microstructural and mechanical properties of Al-Zn-Mg-Cu P/M alloy
Prediction of low-cycle fatigue-life by acoustic emission—1: 2024-T3 aluminum alloy, and —2: 7075-T6 aluminum alloy
Intergranular corrosion resistance of Zn modified 5××× series Al alloy during retrogression and re-aging treatment
Journal Article
·
Fri May 15 00:00:00 EDT 2015
· AIP Conference Proceedings
·
OSTI ID:20632898
+2 more
Prediction of low-cycle fatigue-life by acoustic emission—1: 2024-T3 aluminum alloy, and —2: 7075-T6 aluminum alloy
Journal Article
·
Thu Jan 01 00:00:00 EST 1981
· Engineering Fracture Mechanics
·
OSTI ID:20632898
Intergranular corrosion resistance of Zn modified 5××× series Al alloy during retrogression and re-aging treatment
Journal Article
·
Mon Oct 15 00:00:00 EDT 2018
· Materials Characterization
·
OSTI ID:20632898
+1 more